Abstract:The choice of support and catalyst materials has been proved to be critical to scalable chemical vapor deposition (CVD) synthesis of carbon nanotubes. In our study, we found that porous MgO prepared by thermal decomposition of its salts was an eminent support material for CVD growth of single-walled carbon nanotubes (SWNTs). Compared with other kinds of supports such as SiO2, ZrO2,Al2O3 and CaO etc., the quality of as-grown SWNTs on MgO supports was stable; the effects of reaction conditions such as furnace temperature, flow rate of the gas and the types of catalysts and supports on the properties of as-prepared SWNT products were thoroughly investigated and characterized by micro-Raman spectroscopy, transmission electron microscopy (TEM), scanning electron microscopy (SEM) and thermogravimetry (TG) techniques. The results indicated that the yields of SWNTs on MgO supports could be up to about 120% with the addition of a small amount of assistant catalyst Mo salt. The obtained purity of the as-grown products was higher than 90% after treatment with 4 M HCl. The obvious advantages of using MgO supports include efficient and stable growth of SWNTs, scalable synthesis of SWNTs at low cost, and easy removal of the support in mild acid, causing little harm to the products.

Synthesis Of High Quality Single-Walled Carbon Nanotubes By Cvd And Effect Of Catalyst'S Acidity-Basicity On Nanotubes Growth

Controlling the Diameters in Large-Scale Synthesis of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

Cvd Synthesis and Diameter Distribution of Single-Walled Carbon Nanotubes

Large- Scale Production of Single- Walled Carbon Nanotubes Using Fe/Mo/MgO Cryogel Catalyst

CVD synthesis of single-walled carbon nanotubes by Co/MgO solid catalysts

Synthesis of Carbon Nanotubes by Decomposing Alcohol

Possible Tactics to Improve the Growth of Single-Walled Carbon Nanotubes by Chemical Vapor Deposition

Controlled Growth of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4 over Mo/Co/MgO Catalysts

Ni-Mobi-Metallic Oxide Catalyst for Large-Scale Synthesis of Bundled Multi-Walled Carbon Nanotubes by Cvd

Synthesis of Single-Walled Carbon Nanotubes with Narrow Diameter Distribution by Calcination of a Mo-Modified Fe/MgO Catalyst

A Scalable CVD Synthesis of High-Purity Single-Walled Carbon Nanotubes with Porous MgO As Support Material

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Pii: s0008-6223(02)00175-6

Subnanometer Single-Walled Carbon Nanotube Growth from Fe-Containing Layered Double Hydroxides

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Effect of Carrier Gas on Quality of Cvd Synthesized Carbon Nano-Materials over High Performance Co/Mgmoo4 Catalyst

Very High-Quality Single-Walled Carbon Nanotubes Grown Using a Structured and Tunable Porous Fe/MgO Catalyst

Preparation of Short Single Walled Carbon Nanotubes by CVD Growth and by Chemical Oxidation

Purification and Characterization of Single-Walled Carbon Nanotubes Synthesized by Chemical Vapor Deposition