Abstract:Multi-walled carbon nanotubes (MW-CNTs) were prepared by chemical vapor deposition (CVD) method with the decomposition of acetylene over Co/SiO2 catalyst. TG - DTA technique was used together with TEM and XRD to study the effect of reaction temperature on the composition, graphitized extent, and diameter distribution of the produced raw CNTs based on their oxidization resistance. During the decomposition, the micro-crystallite of the active constituent (Co/SiO2) were growing up 6 the reaction temperature rising. This in turn resulted in an increase of the diameter distribution range of produced MW-CNTs. The average diameter increased from 20 similar to 30 nm (650degreesC) to 30 similar to 50 nm (750degreesC). XRD results also showed the graphitized extent of MW-CNTs was enhanced meanwhile the spacing between the layers (d(002)) decreased from 3.45 Angstrom (650degreesC) to 3.32 Angstrom (850degreesC) with the reaction temperature raised. TG - DTA data showed that the exothermic peak of the amorphous carbon was below 380degreesC and its content would decrease as temperature increasing. In summary, for CVD production of CNTs using acetylene gas on Co/SiO2 catalyst, low temperature (about 650degreesC) favored producing thinner MW-CNTs with the diameter from 20 to 30 nm while higher temperature (about 850degreesC) is favored thicker MW-CNTs (diameter from 70 to 100 nm).

Effect of Carrier Gas on Quality of Cvd Synthesized Carbon Nano-Materials over High Performance Co/Mgmoo4 Catalyst

Methane Catalytic Cracking to Make Hydrogen and Graphitic Nano Carbons (nanotubes, Microfibers, Microballs, Onions) with Zero Emission

Ni-Mobi-Metallic Oxide Catalyst for Large-Scale Synthesis of Bundled Multi-Walled Carbon Nanotubes by Cvd

Synthesis Of High Quality Single-Walled Carbon Nanotubes By Cvd And Effect Of Catalyst'S Acidity-Basicity On Nanotubes Growth

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Effect of Mo-Doping on the Sol-Gel Prepared Catalysts for Synthesizing Multi-Wall Carbon Nanotube Bundles

Magnesium and molybdenum oxide for bundled multi-walled carbon

Synthesis of High-Purity Carbon Nanotubes Bundles from CCVD Method

Synthesis Of Close-Packed Multi-Walled Carbon Nanotube Bundles Using Mo As Catalyst

Mass Production of High-Quality Multi-Walled Carbon Nanotube Bundles on a Ni/Mo/MgO Catalyst

Synthesis of high-quality double-walled carbon nanotubes using porous MgO nanowire supported iron oxide as catalyst

Effect of Temperature, Pressure, and Gas Ratio of Methane to Hydrogen on the Synthesis of Double-Walled Carbon Nanotubes by Chemical Vapour Deposition

Thermogravimetric analysis and TEM characterization of the oxidation and defect sites of carbon nanotubes synthesized by CVD of methane

Application Of Thermogravimetry And Differential Thermal Analysis In Catalytic Cvd Synthesis Of Carbon Nanotubes - Effect Of Reaction Temperature On The Production Of Carbon Nanotubes

Synthesis of Multi-Walled Carbon Nanotubes Using Comnmgo Catalysts Through Catalytic Chemical Vapor Deposition

Effect of Hydrocarbons Precursors on the Formation of Carbon Nanotubes in Chemical Vapor Deposition

Controlled Growth of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4 over Mo/Co/MgO Catalysts

Large-scale CVD synthesis of nitrogen-doped multi-walled carbon nanotubes with controllable nitrogen content on a CoxMg1-xMoO4 catalyst

CVD synthesis of single-walled carbon nanotubes by Co/MgO solid catalysts

Catalysts effect on morphology of carbon nanotubes prepared by catalytic chemical vapor deposition in a nano-agglomerate bed

Solid Single Phase Catalyst for Growth of Bundled or Dispersed MWCNT by CVD