Abstract:Based on the analysis of catalyst particle formation and carbon nanotube (CNT) array growth process in floating catalyst chemical vapor deposition (CVD), delicately controlled gaseous carbon sources and catalyst precursors were introduced into the reactor for the controllable growth of CNT array. The low feeding rate of ferrocene was realized through low-temperature sublimation. With less ferrocene introduced into the reactor, the collision among the in situ formed iron atoms decreased, which led to the formation of smaller catalyst particles. The mean diameter of the CNT array, grown at 800(o)C, decreased from 41 to 31 nm when the ferrocene-sublimed temperature reduced from 80 to 60(o)C. Furthermore, low growth temperature was adopted in synthesis, through the modulation of the CNT diameter, by controlling the sintering of catalyst particles and the collision frequency. When the growth temperature was 600(o)C, the as-grown CNTs in the array were with a mean diameter of 10.2 nm. If propylene was used as carbon source, the diameter can be modulated in similar trends. The diameter of CNT can be modulated by the parameter of the operation using the same substrate and catalyst precursor without other equipment or previous treatment. Those results provide the possibility for delicately controllable synthesis of CNT array via simple floating catalyst CVD.

Producing Carbon Nanotube Powder in A Floating Iron Catalyst Lpcvd System

In-situ Synthesis of Fe-filled Carbon Nanotubes by a Floating CVD Method with FeCl3 As Catalyst Precursor

Preparation of carbon nanofibers by the floating catalyst method

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Preparation of High Purity Carbon Nano -Tubes from Ethylene Decomposition over Nanosized Iron- Based Catalysts

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Chemical Vapor Deposition and Synthesis on Carbon Nanofibers: Sintering of Ferrocene-Derived Supported Iron Nanoparticles and the Catalytic Growth of Secondary Carbon Nanofibers

Double wall carbon nanotubes promoted by sulfur in a floating iron catalyst CVD system

Synthesis of Single-Walled Carbon Nanotubes by the Vertical Floating Catalyst Method

Catalytic Growth of Multi-Wall Carbon Nanotubes on Carbon Cloth Using Powdery Ferrous Sulfate Heptahydrate As Catalyst Precursor

Controllable growth of double wall carbon nanotubes in a floating catalytic system

Catalyst Design Using Nanoporous Iron for the Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes

Producing cleaner double-walled carbon nanotubes in a floating catalyst system

Modulating the Diameter of Carbon Nanotubes in Array Form Via Floating Catalyst Chemical Vapor Deposition

Catalyst Effect on the Preparation of Single-Walled Carbon Nanotubes by a Modified Arc Discharge

Controllable Fabrication of Carbon Nanotubes on Catalystic Nanoparticles Derived from Block Copolymer Micelles

Co-synthesis of Single-Walled Carbon Nanotubes and Carbon Fibers

Growth of Branch Carbon Nanotubes on Carbon Nanotubes As Support

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Large- Scale Production of Single- Walled Carbon Nanotubes Using Fe/Mo/MgO Cryogel Catalyst

Growth of Carbon Nanotubes on Si Substrate Using Fe Catalyst Produced by Pulsed Laser Deposition.