Abstract:Undoped and Er-doped NaY(WO4)2 disordered single crystals have been grown by the Czochralski technique. The specific heat and thermal conductivity (κ) of these crystals have been characterized from T = 4 K to 700 K and 360 K, respectively. It is shown that κ exhibits anisotropy characteristic of single crystals as well as a κ(T) behavior observed in glasses, with a saturation mean free phonon path of 3.6 Å and 4.5 Å for propagation along a and c crystal axes, respectively. The relative energy positions and irreducible representations of Stark Er(3+) levels up to (4)G(7/2) multiplet have been determined by the combination of experimental low (<10 K) temperature optical absorption and photoluminescence measurements and simulations with a single-electron Hamiltonian including both free-ion and crystal field interactions. Absorption, emission and gain cross sections of the (4)I(13/2)↔(4)I(15/2) laser related transition have been determined at 77 K. The (4)I(13/2) Er(3+) lifetime (τ) was measured in the temperature range of 77-300 K, and was found to change from τ (77K) ≈ 4.5 ms to τ (300K) ≈ 3.5 ms. Laser operation is demonstrated at 77 K and 300 K by resonantly pumping the (4)I(13/2) multiplet at λ≈1500 nm with a broadband (FWHM≈20 nm) diode laser source perfectly matching the 77 K crystal (4)I(15/2) → (4)I(13/2) absorption profile. At 77 K as much as 5.5 W of output power were obtained in π-polarized configuration with a slope efficiency versus absorbed pump power of 57%, the free running laser wavelength in air was λ≈1611 nm with the laser output bandwidth of 3.5 nm. The laser emission was tunable over 30.7 nm, from 1590.7 nm to 1621.4 nm, for the same π-polarized configuration.

Analysis of Optical Waveguide Formation in Er:NaY(WO4)2 Crystal by MeV He+ Ion Implantation

Monomode Optical Planar and Channel Waveguides in Yb3+-doped Silicate Glasses Formed by Helium Ion Implantation

Planar waveguides in neodymium-doped calcium niobium gallium garnet crystals produced by proton implantation

Monomode Optical Waveguides in Yb3+-Doped Silicate Glasses Produced by Low-Dose Carbon Ion Implantation

One-dimensional and two-dimensional Er 3+ -doped germanate glass waveguides by combination of He + ion implantation and precise diamond blade dicing

Low-dose carbon-implanted planar waveguides in Er 3+ /Yb 3+ co-doped silicate glasses

Optical Properties of Yb3+-doped Silicate Glasses Waveguides Formed by Low-Dose Oxygen Ion Implantation and Effects of Annealing

Oxygen-implanted optical planar waveguides in Er3+/Yb3+-codoped silicate glasses for integrated laser generation

Planar Optical Waveguides in KNbO 3 Formed by MeV B and He Ion Implantation

Transparent Ho,Yb:YAG crystal waveguide inscribed by direct femtosecond laser writing

Thermal characterization, crystal field analysis and in-band pumped laser performance of Er doped NaY(WO(4))(2) disordered laser crystals

Lattice Damage, Optical and Electrical Properties Induced by H and C Ions Implantation in Nd:YLF Crystals

Optical Planar Waveguides in Yb 3+ -Doped Phosphate Glasses Produced by He + Ion Implantation

Enhanced Raman intensity in ZnS planar and channel waveguide structures via carbon ion implantation

Formation of Optical Waveguide and Annealing Behaviour of LiNbO 3 Implanted by 3.0-Mev Nickel Ions

MeV Ti ion-implantation-induced damages in LiNbO3

Optical Amplification in Er/Yb Silicate Strip Loaded Waveguide

Optical amplification in Er/Yb silicate slot waveguide.

Fabrication and Annealing Optimization of Oxygen-Implanted Yb3+-doped Phosphate Glass Planar Waveguides

Optical properties of the O3+-ion implanted and femtosecond-laser ablated ridge waveguide in the Er3+-doped germanate glass

E r silicate nanowire light source for silicon photonics