Abstract:The optically polished LiNbO3 crystal was implanted with 3.0 MeV nickel ions to a dose of 8 x 1014 ions/cm(2). The implanted sample was orderly annealed at different temperatures for different times in air ambient. The waveguide properties before and after annealing were investigated. Dark modes were observed by the prism coupling technique. The reconstructed refractive index profiles were obtained with the reflectivity calculation method. With the fibre probe technique, the attenuation of the Ni-implanted barrier-confined waveguide was measured for the first time. The waveguide loss was reduced from 1.65dB/cm to 1.19dB/cm when annealing was at 300degreesC for 30 min. With the annealing temperature increasing to 370degreesC, only fewer broad dark modes were found. It is indicated that the lattice damage by implantation began to resume under this annealing condition. After annealing at 380degreesC for 60 min, all the dark modes disappeared.

Planar Optical Waveguides In Knbo3 Formed By Mev B And He Ion Implantation

Formation of optical waveguides in KNbO3 by MeV boron ion implantation

MeV Ti ion-implantation-induced damages in LiNbO3

Modal Characterization of a Planar Waveguide in Bismuth Borate Crystal

Second harmonic and raman imaging of He+ implanted KTiOPO4 waveguides

Planar waveguides in neodymium-doped calcium niobium gallium garnet crystals produced by proton implantation

Monomode Optical Planar and Channel Waveguides in Yb3+-doped Silicate Glasses Formed by Helium Ion Implantation

Near-infrared Carbon-Implanted Waveguides in Tb3+-doped Aluminum Borosilicate Glasses

Optical Planar Waveguides in Yb 3+ -Doped Phosphate Glasses Produced by He + Ion Implantation

MgO:LiNbO3 Planar Waveguide Formed by MeV O2+ Implantation and Its Annealing Characteristics

Formation of Optical Waveguide and Annealing Behaviour of LiNbO 3 Implanted by 3.0-Mev Nickel Ions

Monomode Optical Waveguides in Yb3+-Doped Silicate Glasses Produced by Low-Dose Carbon Ion Implantation

Helium-Implanted Optical Planar Waveguides in Nd <sup>3+</sup> -Doped Phosphate Glass

Fabrication and Characterization of Ion-Exchanged Optical Waveguides in Potassium Lithium Niobate Crystal Substrates

Helium-implanted optical planar waveguides in Nd3+-doped phosphate glass

Enhanced Raman intensity in ZnS planar and channel waveguide structures via carbon ion implantation

OBSERVATION OF PHOTOREFRACTIVE EFFECT OF KNbO 3 CRYSTAL AT μW ILLUMINATION

Planar waveguide nanolaser configured by dye-doped hybrid nanofilm on substrate

Fabrication and characteristics of the C3+‐ion implanted and femtosecond‐laser ablated RTP 2D waveguide

Visible and near-infrared optical properties of a proton-implanted KTP waveguide

Planar and ridged waveguide preparation on erbium pre-implanted fused silica by multi-energy helium ion implantation and femtosecond laser ablation