Abstract:The symmetrical optical waveguide structures are fabricated in Er3+-doped aluminosilicate glass using 800 nm femtosecond laser writing in kHz repetition frequency regime. The impact of writing parameters on the waveguide preparation with a 10× microscope objective in the longitudinal writing scheme was studied in detail. The experimental results show that, under a fixed pulse energy value of 20 μJ, the waveguides can be realized with the scan speed from 20 to 160 μm/s, and with a fixed scan speed value of 160 μm/s, the waveguide can be prepared under an inscription energy range of 5–30 μJ, indicating that the waveguide can be realized in a wide range of writing parameters. The near-field mode intensity image shows that the waveguide region possesses excellent light guiding properties. Based on the refractive index profile reconstruction method, the maximum refractive index increase in the waveguide region is estimated to be about 5.5 × 10–4. The lowest propagation loss of the waveguide was measured to be about 1.51 dB/cm by the waveguide side scattering method. The microfluorescence spectra show that the gain characteristics of the waveguide region are well maintained after laser processing. This work shows that the fabrication of embedded optical waveguides using ultrashort pulse laser in Er3+-doped aluminosilicate glass has strong feasibility and great potential to create active gain devices in the field of integrated photonics and all-optical communication.

Low-dose carbon-implanted planar waveguides in Er 3+ /Yb 3+ co-doped silicate glasses

Monomode Optical Waveguides in Yb3+-Doped Silicate Glasses Produced by Low-Dose Carbon Ion Implantation

Oxygen-implanted optical planar waveguides in Er3+/Yb3+-codoped silicate glasses for integrated laser generation

Monomode Optical Planar and Channel Waveguides in Yb3+-doped Silicate Glasses Formed by Helium Ion Implantation

Proton-Implanted Optical Planar Waveguides in Yb3+-Doped Silicate Glasses

Optical Properties of Yb3+-doped Silicate Glasses Waveguides Formed by Low-Dose Oxygen Ion Implantation and Effects of Annealing

Optical Planar Waveguides in Yb 3+ -Doped Phosphate Glasses Produced by He + Ion Implantation

Fabrication and Annealing Optimization of Oxygen-Implanted Yb3+-doped Phosphate Glass Planar Waveguides

Helium-implanted optical planar waveguides in Nd3+-doped phosphate glass

Near-infrared Carbon-Implanted Waveguides in Tb3+-doped Aluminum Borosilicate Glasses

Erbium-ytterbium co-doped aluminium oxide waveguide amplifiers fabricated by reactive co-sputtering and wet chemical etching

Guided-Wave Up-Conversion Luminescence in Er3+/Yb3+ Co-doped Phosphate Glass Waveguide Produced by Direct Femtosecond Laser Writing

Planar waveguides in neodymium-doped calcium niobium gallium garnet crystals produced by proton implantation

One-dimensional and two-dimensional Er 3+ -doped germanate glass waveguides by combination of He + ion implantation and precise diamond blade dicing

Planar waveguide nanolaser configured by dye-doped hybrid nanofilm on substrate

Analysis of Optical Waveguide Formed in X-Cut Yb:GdCOB Crystal by He+ Implantation

Helium-Implanted Optical Planar Waveguides in Nd <sup>3+</sup> -Doped Phosphate Glass

Investigation of Optical Waveguide Formed in Er:Yb:phosphate Glass by MeV He+ Implantation

Study on Er3+-Yb3+ co-doped La2O3–Al2O3 glasses for C-band optical waveguide amplifier with high luminous efficiency and low pump threshold

Direct Writing of Channel Optical Waveguides in Er 3+ -Doped Aluminosilicate Glass by Low Repetition Rate Femtosecond Laser

Light-induced self-written waveguides based on NaYF4/polymer composites for the C-band amplification