Abstract:The symmetrical optical waveguide structures are fabricated in Er3+-doped aluminosilicate glass using 800 nm femtosecond laser writing in kHz repetition frequency regime. The impact of writing parameters on the waveguide preparation with a 10× microscope objective in the longitudinal writing scheme was studied in detail. The experimental results show that, under a fixed pulse energy value of 20 μJ, the waveguides can be realized with the scan speed from 20 to 160 μm/s, and with a fixed scan speed value of 160 μm/s, the waveguide can be prepared under an inscription energy range of 5–30 μJ, indicating that the waveguide can be realized in a wide range of writing parameters. The near-field mode intensity image shows that the waveguide region possesses excellent light guiding properties. Based on the refractive index profile reconstruction method, the maximum refractive index increase in the waveguide region is estimated to be about 5.5 × 10–4. The lowest propagation loss of the waveguide was measured to be about 1.51 dB/cm by the waveguide side scattering method. The microfluorescence spectra show that the gain characteristics of the waveguide region are well maintained after laser processing. This work shows that the fabrication of embedded optical waveguides using ultrashort pulse laser in Er3+-doped aluminosilicate glass has strong feasibility and great potential to create active gain devices in the field of integrated photonics and all-optical communication.

The structural and refractive index changes in the waveguides written by femtosecond laser in Er-doped silicate glasses

Optical loss measurements in femtosecond laser written waveguides in glass

Femtosecond laser writing low-loss waveguides in silica glass: highly symmetrical mode field and mechanism of refractive index change

Femtosecond laser direct written waveguides and laser induced-effects in erbium-doped GYSGG crystals

Optical Waveguides Induced in Inorganic Glasses by a Femtosecond Laser

Direct Writing of Channel Optical Waveguides in Er 3+ -Doped Aluminosilicate Glass by Low Repetition Rate Femtosecond Laser

Influence of Focusing Depth on the Microfabrication of Waveguides Inside Silica Glass by Femtosecond Laser Direct Writing

Densification of silica glass induced by 0.8 and 1.5μm intense femtosecond laser pulses

Optical Waveguide Writing Inside Foturan Glass with Femtosecond Laser Pulses

1550-Nm Light Amplification from Erbium-Doped Silica Glass Waveguide Written by Femtosecond Laser Pulses

Optical and fluorescent properties in Er, Yb:YAG double-line waveguide by femtosecond laser direct writing

Fabrication of High Refractive Index-Modulation Structures in Fused Silica by Femtosecond Laser Pulses

Infrared photosensitivity in silica glasses exposed to femtosecond laser pulses

Transparent Ho,Yb:YAG crystal waveguide inscribed by direct femtosecond laser writing

Bending Loss in Mid-Infrared Waveguides and Fibers

Three-dimensional microscopic modifications in glasses by a femtosecond laser

The influence of femtosecond laser wavelength on waveguide fabrication inside fused silica

Oxygen-implanted optical planar waveguides in Er3+/Yb3+-codoped silicate glasses for integrated laser generation

Effectively Writing Low Propagation and Bend Loss Waveguides in the Silica Glass by Using a Femtosecond Laser.

Photowritten Optical Waveguides in Various Glasses with Ultrashort Pulse Laser

Femtosecond Laser Modification of Silica Optical Waveguides for Potential Bragg Gratings Sensing