Abstract:The symmetrical optical waveguide structures are fabricated in Er3+-doped aluminosilicate glass using 800 nm femtosecond laser writing in kHz repetition frequency regime. The impact of writing parameters on the waveguide preparation with a 10× microscope objective in the longitudinal writing scheme was studied in detail. The experimental results show that, under a fixed pulse energy value of 20 μJ, the waveguides can be realized with the scan speed from 20 to 160 μm/s, and with a fixed scan speed value of 160 μm/s, the waveguide can be prepared under an inscription energy range of 5–30 μJ, indicating that the waveguide can be realized in a wide range of writing parameters. The near-field mode intensity image shows that the waveguide region possesses excellent light guiding properties. Based on the refractive index profile reconstruction method, the maximum refractive index increase in the waveguide region is estimated to be about 5.5 × 10–4. The lowest propagation loss of the waveguide was measured to be about 1.51 dB/cm by the waveguide side scattering method. The microfluorescence spectra show that the gain characteristics of the waveguide region are well maintained after laser processing. This work shows that the fabrication of embedded optical waveguides using ultrashort pulse laser in Er3+-doped aluminosilicate glass has strong feasibility and great potential to create active gain devices in the field of integrated photonics and all-optical communication.

Optical Waveguide Writing Inside Foturan Glass with Femtosecond Laser Pulses

Optical loss measurements in femtosecond laser written waveguides in glass

Fabrication of Optical Cavities with Femtosecond Laser Pulses

Transverse writing of three-dimensional tubular optical waveguides in glass with a slit-shaped femtosecond laser beam

Low-loss optofluidic waveguides in fused silica enabled by spatially shaped femtosecond laser assisted etching combined with carbon dioxide laser irradiation

Transverse writing of three-dimensional tubular optical waveguides in glass with slit-shaped femtosecond laser beams

Optical Waveguides Induced in Inorganic Glasses by a Femtosecond Laser

Mode-tunable Low-Loss Waveguides in Glass for Visible Light Photonic Integrated Devices

Fabrication of micro-optical components by using a femtosecond laser

Photowritten Optical Waveguides in Various Glasses with Ultrashort Pulse Laser

Influence of Focusing Depth on the Microfabrication of Waveguides Inside Silica Glass by Femtosecond Laser Direct Writing

Femtosecond laser writing low-loss waveguides in silica glass: highly symmetrical mode field and mechanism of refractive index change

Direct Writing of Channel Optical Waveguides in Er 3+ -Doped Aluminosilicate Glass by Low Repetition Rate Femtosecond Laser

Effectively Writing Low Propagation and Bend Loss Waveguides in the Silica Glass by Using a Femtosecond Laser.

Single-step fabrication of surface waveguides in fused silica with few-cycle laser pulses

Transverse Writing of Multimode Interference Waveguides Inside Silica Glass by Femtosecond Laser Pulses

Femtosecond laser direct writing device and femtosecond laser direct writing method for annular waveguide in transparent materials

Fabricating Low Loss Waveguides over a Large Depth in Glass by Temperature Gradient Assisted Femtosecond Laser Writing.

The structural and refractive index changes in the waveguides written by femtosecond laser in Er-doped silicate glasses

Photonic Circuits Written by Femtosecond Laser in Glass: Improved Fabrication and Recent Progress in Photonic Devices

Femtosecond laser written low-loss multiscan waveguides in fused silica