Abstract:The symmetrical optical waveguide structures are fabricated in Er3+-doped aluminosilicate glass using 800 nm femtosecond laser writing in kHz repetition frequency regime. The impact of writing parameters on the waveguide preparation with a 10× microscope objective in the longitudinal writing scheme was studied in detail. The experimental results show that, under a fixed pulse energy value of 20 μJ, the waveguides can be realized with the scan speed from 20 to 160 μm/s, and with a fixed scan speed value of 160 μm/s, the waveguide can be prepared under an inscription energy range of 5–30 μJ, indicating that the waveguide can be realized in a wide range of writing parameters. The near-field mode intensity image shows that the waveguide region possesses excellent light guiding properties. Based on the refractive index profile reconstruction method, the maximum refractive index increase in the waveguide region is estimated to be about 5.5 × 10–4. The lowest propagation loss of the waveguide was measured to be about 1.51 dB/cm by the waveguide side scattering method. The microfluorescence spectra show that the gain characteristics of the waveguide region are well maintained after laser processing. This work shows that the fabrication of embedded optical waveguides using ultrashort pulse laser in Er3+-doped aluminosilicate glass has strong feasibility and great potential to create active gain devices in the field of integrated photonics and all-optical communication.

Optical Waveguides Induced in Inorganic Glasses by a Femtosecond Laser

Photowritten Optical Waveguides in Various Glasses with Ultrashort Pulse Laser

Optical loss measurements in femtosecond laser written waveguides in glass

Three-dimensional microscopic modifications in glasses by a femtosecond laser

Optical Waveguide Writing Inside Foturan Glass with Femtosecond Laser Pulses

The structural and refractive index changes in the waveguides written by femtosecond laser in Er-doped silicate glasses

Space-selective Microscopic Modifications of Glass Structure by a Femtosecond Laser

Direct laser-writing of ferroelectric single-crystal waveguide architectures in glass for 3D integrated optics

Laser Fabrication of Photorefractive Bragg Reflectors, Asymmetric Waveguides and Void Arrays in Glass

Direct Writing of Channel Optical Waveguides in Er 3+ -Doped Aluminosilicate Glass by Low Repetition Rate Femtosecond Laser

Femtosecond laser direct writing of multiwavelength Bragg grating waveguides in glass

Femtosecond laser direct written waveguides and laser induced-effects in erbium-doped GYSGG crystals

Femtosecond laser-induced microstructures in glasses and applications in micro-optics.

Fabrication of micro-optical components by using a femtosecond laser

Mechanisms and Applications of Femtosecond Laser Induced Nanostructures

Ultrafast Laser-Fabricated Fluoride Glass Waveguides with Exceptionally High Refractive Index Change for Mid-Infrared Integrated Optics

Infrared photosensitivity in silica glasses exposed to femtosecond laser pulses

Ultrafast Laser Inscription of High Performance Mid-Infrared Waveguides in Chalcogenide Glass

Ultrafast laser inscribed waveguides in tailored fluoride glasses: an enabling technology for mid-infrared integrated photonics devices

Single-scan Ultrafast Laser Inscription of Waveguides in IG2 for Type-I and Type-Ii Operation in the Mid-Infrared.

Femtosecond Laser-Induced Microfeatures in Glasses and Their Applications