Abstract:A new way on the magnitude and position of direction change of shear deformation resulted from rolling geometry and friction described by two parameters of Rf and Rp changed with practical rolling conditions is established for analyzing rolling textures. It is found that {001} <110> shear texture is dependent on the parameters of Rf and Rp, and rolling neutral angle is at the middle point of rolling deformation zone, i.e. Rp = 0.5, which favors development of {001}<110> shear texture. The results show that the rolling textures simulated by taking into account of Rf and Rp changed with practical rolling conditions are in better agreement with the measured than that of Rp = 0.5 in rolled high purity Al. Introduction Rolling textures and deformation microstructures have been demonstrated to be changed with rolling geometry and friction on contact surfaces between rollers and sample in previous investigations [1, 2, 3], in which {001}<110> shear texture and micro-shear bands with Cube orientation were found in rolled high purity aluminum with heavier rolling friction. However, the presented ways on effect of rolling geometry and friction on rolling texture components were either simple or complex, and rolling neutral angle position was hypothesized to be at the middle point of rolling deformation zone (RDZ) in literatures [4, 5, 6]. In current investigation, shear deformation can conventionally be changed with practical rolling conditions including rolling geometry and friction, especially, the position of direction change of shear deformation, i.e., rolling neutral angle, is not hypothesized to be at the middle point of RDZ per pass. Development of rolling textures in high purity Al rolled up to different total engineering strains is studied by experiment and modeling. Application of practical conditions on rolling texture modeling Practical Rolling conditions. All that rolling conditions are constrained by three angles, α, β and γ, and a relationship of the three angles can be described as known as

Friction and Slab Deformation Behaviour During Rough Rolling

Evolution of Residual Stress Based on Curvature Coupling in Multi-Roll Levelling

Evolution of Surface Crack on Slab During Rough Rolling Using Thermal-Mechanical FEM

The Cracks on Slab Corner During Hot Rolling Process

Influence of Groove Fillet Radii of Edger Roll on Slab Deformation

Crystal Plasticity Finite Element Simulation of Grain Evolution Behavior in Aluminum Alloy Rolling

FINITE ELEMENT ANALYSIS OF STEADY STATE HV ROLLING PROCESS OF SLAB

An Efficient Multi-Scale Modeling Method that Reveals Coupled Effects Between Surface Roughness and Roll-Stack Deformation in Cold Sheet Rolling

Finite Element Analysis of Temper Rolling Process

Coupling effect of plastic deformation and surface roughness on friction behaviors of rough line contact for ground metal surfaces

Tri-dimensional Elastic-Plastic Fem of Rolling Force During Strip Finishing Rolling Process

Effect of three types of driving modes of rolling mill with six rolls on the friction force between rolls

The effect of oxide scale of stainless steels on friction and surface roughness in hot rolling

Surface plastic deformation distribution and microstructural evolution in the compound rolling of Ti–50Al billet

Mechanics characteristics of surface damage on sliding-rolling friction pair under high-speed and heavy-load condition

Influence of Roll Smoothing on the Initial Residual Stress Fields of 10ni5crmov Steel Heavy Gauge Plates

Coulomb, Tresca and Coulomb-Tresca Friction Models Used in Analytical Analysis for Rolling Process of External Spline

Effect of Direction Change of Shear Deformation on the Textures in Rolled High Purity Al

SIMULATION OF STEADY STATE SLAB EDGING WITH 3D RIGID-PLASTIC FEM

Effect of hot rolling process parameters on surface wear of descaling rolls

Digital simulation of aluminum alloy slab rolling with low relative reduction