Test of Cl- and SO42- in Concrete Exposed to Composite Salt Environment by Conductivity Titration
Dafu Wang,Yue Li,Yunsheng Zhang,Zhiyong Liu,Yidong Chen,Cheng Liu,Bo Pang,Jun Ren,Zhiyong Xie
DOI: https://doi.org/10.1016/j.conbuildmat.2024.137525
IF: 7.4
2024-01-01
Construction and Building Materials
Abstract:Concrete structures are usually exposed to the corrosive environment with Cl- and SO42-. However, testing Cl- and SO42- in a composite solution dissolved from corroded concrete is difficult. For this purpose, the Cl- and SO42- test method in composite solution was investigated through the titration models and the experimental tests. The results show that the conductivity titration can accurately test Cl- and SO42- in the composite solution dissolved from corroded concrete. To avoid the effect of Cl- during the titration of SO42-, Ba(NO3)2 is chosen as the titrant for the titration of SO42-. The titration endpoint for the test of Cl- is easier to determine than that of SO42- since the solubility of AgCl is much smaller than that of BaSO4. When SO42- with a lower concentration in a composite solution cannot generate precipitation of Ag2SO4 during the titration of Cl-, the titration order for Cl- and SO42- does not affect their titration results. However, when the concentration of SO42- is larger, titration of SO42- should be performed before titrating Cl- in the same measured solution. In the free Cl- and SO42- test in cementitious materials, OH- and CO32- should be eliminated by adding HNO3 to avoid generating AgOH, Ag2CO3, and BaCO3. In the total Cl- and SO42- test, the titration of Cl- and SO42- should be separately performed due to the presence of other ions with high conductivity. In the test of total SO42-, HCl is used to dissolve the cement-based material, whereas Ag2O and CO2 are used to eliminate Ca2+, Cl-, and H+. In the test of total Cl-, H2SO4 is used to dissolve the cement-based material, whereas BaO and CO2 are used to eliminate Ca2+, SO42-, and H+.