Abstract:In order to study the durability of concrete materials subjected to sulfate attack, in a sulfate attack environment, a series of concrete tests considering different fly ash contents and erosion times were conducted. The mechanical properties and the micro-structure of concrete under sulfate attack were studied based on the following: uniaxial compressive strength test, split tensile test, ultrasonic impulse method, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The mechanical properties were compressive strength, splitting tensile strength, and relative dynamic elastic modulus, respectively. Additionally, according to the damage mechanical theory, experimental results and micro-structure analysis, the damage evolution process of concrete under a sulfate attack environment were studied in detail. Finally, according to the sulfate attack time and fly ash content, a damage model of the sulfate attack of the binary surface was established. The specific results are as follows: under the action of sulfate attack, the change law of the rate of mass change, relative dynamic modulus of elasticity, corrosion resistance coefficient of compressive strength, and the corrosion resistance coefficient of the splitting tensile strength of concrete all increase first and then decrease. Under the same erosion time, concrete mixed with 10% fly ash content has the best sulfate resistance. Through data regression, the damage evolution equation of the sulfate attack was developed and there is an exponential function relationship among the different damage variables. The binary curved surface regression effect of the concrete damage and the erosion time and the amount of fly ash is significant, which can predict deterioration of concrete damage under sulfate attack. During the erosion time, the combined expansion of ettringite and gypsum caused micro cracks. With an increase of corrosion time, micro cracks developed and their numbers increased.

Degradation Mechanism of Concrete Subjected to External Sulfate Attack: Comparison of Different Curing Conditions

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Degradation mechanisms of cast-in-situ concrete subjected to internal-external combined sulfate attack

Partially-exposed cast-in-situ concrete degradation induced by internal-external sulfate and magnesium multiple coupled attack

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Study on Corrosion Mechanism of Different Concentrations of Na2SO4 Solution on Early-Age Cast-In-Situ Concrete

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

Mechanical Properties and Damage Evolution of Concrete Materials Considering Sulfate Attack

Reliability assessment of concrete under external sulfate attack

Mechanism and Performance Control Methods of Sulfate Attack on Concrete: A Review

Accelerating Tests For The Performance Deterioration Of Concrete Exposed To Chloride Media

Study on the Deterioration of Concrete under Dry-Wet Cycle and Sulfate Attack

Study on the deterioration of concrete performance in saline soil area under the combined effect of high low temperatures, chloride and sulfate salts

RESEARCH ON MECHANISM OF SULFATE ATTACK ON CONCRETE BY TG-DSC METHOD

Damage Constitutive Model and Mechanical Performance Deterioration of Concrete under Sulfate Environment

Influence of Ca2+ on Early Degradation of Cast-In-Situ Mortar Induced by Sulfate-Magnesium Multiple Combined Attack

Concrete Deterioration Mechanisms under Combined Sulfate Attack and Flexural Loading

Decay of fracture parameters of concrete under sulfate environments

Influence of the Initial Moist Curing Time on the Sulfate Attack Resistance of Concretes with Different Binders

Effects of Sodium Sulfate Attack on Concrete Incorporated with Drying-Wetting Cycles