Abstract:In order to study the durability of concrete materials subjected to sulfate attack, in a sulfate attack environment, a series of concrete tests considering different fly ash contents and erosion times were conducted. The mechanical properties and the micro-structure of concrete under sulfate attack were studied based on the following: uniaxial compressive strength test, split tensile test, ultrasonic impulse method, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The mechanical properties were compressive strength, splitting tensile strength, and relative dynamic elastic modulus, respectively. Additionally, according to the damage mechanical theory, experimental results and micro-structure analysis, the damage evolution process of concrete under a sulfate attack environment were studied in detail. Finally, according to the sulfate attack time and fly ash content, a damage model of the sulfate attack of the binary surface was established. The specific results are as follows: under the action of sulfate attack, the change law of the rate of mass change, relative dynamic modulus of elasticity, corrosion resistance coefficient of compressive strength, and the corrosion resistance coefficient of the splitting tensile strength of concrete all increase first and then decrease. Under the same erosion time, concrete mixed with 10% fly ash content has the best sulfate resistance. Through data regression, the damage evolution equation of the sulfate attack was developed and there is an exponential function relationship among the different damage variables. The binary curved surface regression effect of the concrete damage and the erosion time and the amount of fly ash is significant, which can predict deterioration of concrete damage under sulfate attack. During the erosion time, the combined expansion of ettringite and gypsum caused micro cracks. With an increase of corrosion time, micro cracks developed and their numbers increased.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to study the durability of concrete materials in the sulfate - erosion environment and its damage evolution process. Specifically, the paper focuses on the following aspects:
1. **The influence of sulfate erosion on the mechanical properties of concrete**: Through a series of experiments (uniaxial compressive strength test, splitting tensile test, ultrasonic pulse method, etc.), the changes in the mechanical properties of concrete under different fly ash contents and erosion times are studied.
2. **Micro - structure analysis**: Using scanning electron microscopy (SEM) and X - ray diffraction (XRD) techniques, the micro - structure changes of concrete after sulfate erosion are analyzed, and the erosion products and their influence on the performance of concrete are explored.
3. **Establishment of damage evolution model**: Based on damage mechanics theory, combined with experimental results and micro - structure analysis, the damage evolution process of concrete in the sulfate - erosion environment is studied in detail, and a composite damage model considering fly ash content and erosion time is established.
### Specific problem description
- **Sulfate erosion mechanism**: Sulfate erosion refers to the reaction between sulfate ions in the solution and cement hydration products to generate expansive products (such as ettringite) when concrete is immersed in sulfate solution for a long time. These products gradually generate stress on the pore walls inside the concrete, causing concrete deformation and damage, which seriously affects its durability and service life.
- **Deficiencies in existing research**: At present, most scholars mainly study the change rules of the macroscopic mechanical properties of concrete under sulfate erosion and the erosion mechanism, but rarely pay attention to the relationships between various evaluation indicators, and most of them are single - factor models. Therefore, it is necessary to establish a damage model that comprehensively considers erosion time and material components to more comprehensively evaluate the damage evolution process of concrete.
### Research significance
Through this research, the damage mechanism of sulfate erosion on concrete can be better understood, providing theoretical support and experimental basis for improving the durability of concrete structures in sulfate environments, thereby prolonging the service life of structures and reducing economic losses.
### Summary of key formulas
- **Mass change rate**:
\[
\phi_i=\frac{m_n - m_0}{m_0}
\]
where \(\phi_i\) is the mass change rate of the concrete specimen, \(m_n\) is the mass of the specimen after erosion time \(n\), and \(m_0\) is the initial mass.
- **Relative dynamic elastic modulus**:
\[
E_r(n)=\frac{E_n}{E_0}=\left(\frac{v_n}{v_0}\right)^2
\]
where \(E_r(n)\) is the relative dynamic elastic modulus of the concrete specimen, \(E_n\) is the dynamic elastic modulus after erosion time \(n\), \(E_0\) is the initial dynamic elastic modulus; \(v_n\) and \(v_0\) are the longitudinal wave velocities after erosion time \(n\) and the initial ones respectively.
- **Compressive strength corrosion coefficient**:
\[
k_c = \frac{f_{cn}}{f_{c0}}
\]
where \(k_c\) is the compressive strength corrosion coefficient of the concrete specimen, \(f_{cn}\) is the compressive strength after erosion time \(n\), and \(f_{c0}\) is the un - eroded compressive strength.
- **Splitting tensile strength corrosion coefficient**:
\[
k_t=\frac{f_{tn}}{f_{t0}}
\]
where \(k_t\) is the splitting tensile strength corrosion coefficient of the concrete specimen, \(f_{tn}\) is the splitting tensile strength after erosion time \(n\), and \(f_{t0}\) is the un - eroded splitting tensile strength.
Through these formulas, researchers can quantify the influence of sulfate erosion on the performance of concrete and establish corresponding damage evolution models.