Abstract:In this work, the non-uniform corrosion characteristics of steel bars in stressed reinforced concrete beams after accelerated depassivation and seven-year outdoor natural corrosion is analyzed using fractal theory. 3D laser scanning and 3D reconstruction technology are applied to collect the cross-sectional area along the steel bars and obtain the corrosion curves. The non-uniformity of corrosion is analyzed by fractal dimensions which is calculated by variation method. The results indicate that the initial loading level and loading zone have some influence on non-uniform characteristics of steel bars. For an ordinary concrete beam, the increase of load can cause a reduction of fractal dimension of corrosion curves by 5%, which indicates the non-uniformity of corrosion will increase with the increase of load level. The fractal dimension in the bending zone is lower than that in the tension-shear zone, which indicates that corrosion is more non-uniform in bending zone. However, the loading level and loading zone have a slight influence on corrosion level, and the maximum difference of corrosion level caused by load is merely 0.23%. Furthermore, the corrosion level increases with the decrease of fractal dimension, suggesting that the non-uniformity of corrosion increases with the growth of corrosion level. The incorporation of slag powder can help reduce the non-uniformity of corrosion, but the influence on reduction of the corrosion level is about 0.25%. For concrete structures under marine environment, application of slag powder is a good method to slow down the corrosion and reduce the non-uniformity of corrosion.

Applicability Study on Accelerated Corrosion Methods of Steel Bars in Concrete Structure

Study of Wiring Method on Accelerated Corrosion of Steel Bars in Concrete

Study on Experimental Method and Morphology of Accelerated Non-Uniform Corrosion of Steel Bars

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

Applicability of Accelerated Corrosion Method of Steel Bars in Cracked Concrete Structure

Mechanical Performance of Corroded Steel Bars in Concrete

Bond Strength Evaluation of Corroded Steel Bars Via the Surface Crack Width Induced by Reinforcement Corrosion

Evaluation of corrosion morphology on mechanical properties of reinforcing steel bars using numerical simulation and simplified analytical model

A Comparison Study on the Natural and Half-Soaking Galvanic Accelerated Corrosion of Reinforced Concrete Based on an Improved Electrochemical Model

Performance of Reinforced Concrete Beams Corroded under Sustained Service Loads: A Comparative Study of Two Accelerated Corrosion Techniques

The Electrochemical Characterization of Rebar Passivation Film in Simulated Concrete Media

Study On Distribution Of Steel Corrosion Products In Concrete Structures

Distribution of millscale on corroded steel bars and penetration of steel corrosion products in concrete

Study on Corrosion Mechanism of Steel Bars in Concrete and Mechanical Performance of Corroded Steel Bars

Test study on bond behavior of corroded steel bars and concrete

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Effect of Chloride-Induced Reinforcing Steel Corrosion on the Flexural Strength of Reinforced Concrete Beams

Macrocell Corrosion Behavior of Steel Bar with Different Connection

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Corrosion of steel rebar in concrete induced by chloride ions under natural environments

EXPERIMENTAL STUDY ON HOOP BOND BETWEEN CORROSION BAR AND CONCRETE