Abstract:In order to investigate the half-soaking galvanic accelerated corrosion and natural corrosion comparatively, an improved electrochemical model was established. Taking the diffusion of ions, potential distribution and polarization into consideration, the difference between two corrosion methods were essentially revealed. By changing the boundary conditions of the model, Finite Element Method (FEM) was applied to simulate corrosion potential distribution, ions concentration and current density both on the steel–concrete interface and within concrete. In natural corrosion, macrocell corrosion was coupled with microcell corrosion, and the anodic and cathodic current densities were self-balanced. To model the real corrosion under natural environment, the cathodic to anodic area ratio (Ac/Aa) of macrocell was assumed to be changing with the development of corrosion. In galvanic accelerated corrosion, the influence of external ions concentration on current density was considered, which eventually affected the distribution of rust layer of steel rebar. The simulation results agree well with the test data collected from literatures. A further discussion indicates that impressed current density significantly affects the time ratio of natural corrosion to galvanic accelerated corrosion, while the NaCl solution concentration shows no clear influence on time ratio. The bearing capacities of the corroded steel rebar under half-soaking method (HSM) and natural corrosion will show no clear difference, but the HSM method is not very appropriate for studying the corrosion cracking process of reinforced concrete.

Applicability of Accelerated Corrosion Method of Steel Bars in Cracked Concrete Structure

Applicability Study on Accelerated Corrosion Methods of Steel Bars in Concrete Structure

Study of Wiring Method on Accelerated Corrosion of Steel Bars in Concrete

Corrosion-Induced Cracking Propagation Of Rc Beams Subjected To Different Corrosion Methods And Load Levels

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

State-of-art of corrosion-induced cracking of reinforced concrete structures

Bond Strength Evaluation of Corroded Steel Bars Via the Surface Crack Width Induced by Reinforcement Corrosion

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Performance of Reinforced Concrete Beams Corroded under Sustained Service Loads: A Comparative Study of Two Accelerated Corrosion Techniques

Study on Experimental Method and Morphology of Accelerated Non-Uniform Corrosion of Steel Bars

Developing a Three-Dimensional Finite Element Analysis Approach to Simulate Corrosion-Induced Concrete Cracking in Reinforced Concrete Beams

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Mechanical Performance of Corroded Steel Bars in Concrete

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures

Crack Propagation and Flexural Behaviour of Rc Beams under Simultaneous Sustained Loading and Steel Corrosion

Experimental Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Corrosion Characteristics of A 4-Year Naturally Corroded Reinforced Concrete Beam with Load-Induced Transverse Cracks

A Comparison Study on the Natural and Half-Soaking Galvanic Accelerated Corrosion of Reinforced Concrete Based on an Improved Electrochemical Model

On the Penetration of Corrosion Products from Reinforcing Steel into Concrete Due to Chloride-Induced Corrosion

Analysis on steel corrosion at the cracking of concrete