Abstract:Pure colossal dielectric constant oxide CaCu3Ti4O12 (CCTO) compound was prepared by traditional ceramic processing. Dielectric dispersion and complex impedances spectra were investigated using a impedance analyzer within a temperature range of 10-420 K. The data were simulated by "ZVIEW" software. The result indicates that there are two obvious relaxations in the dielectric dispersion spectra when the temperature is higher than room temperature and the dielectric constant increases remarkably with increasing temperatures at a low frequency, which indicates a thermal ionic polarization. However, the frequency spectra becomes similar to Debye-type relaxation when the temperature is lower than room temperature and the low-and high-frequency relaxation step almost keeps unchanged with temperature, which reveals a feature of interface polarization and considerable temperature stability for CCTO. The relaxation revealed in the frequency spectra corresponds to the three different semicircles revealed by the impedance spectra, which indicated there are three inhomogeneous regions or polarization processes in CCTO ceramics and the colossal dielectric constant mainly comes from the extrinsic polarization of these inhomogenities. The activation energies are found to be respectively 0.05 eV, 0.58 eV and 0.49eV for the three different polarization processes by simulating the impedance semicircles using an equivalent circuit.

Dielectric properties and relaxation mechanism of CaCu3Ti4O12 ceramics

Influence of sintering temperature on giant dielectric property of CaCu3Ti4O12

High Capacitance-Temperature Sensitivity and "giant" Dielectric Constant in Srtio3

Ti deficiency effect on the dielectric response of CaCu3Ti4O12 ceramics

Investigation of the Size Effect on the Giant Dielectric Constant of CaCu 3 Ti 4 O 12 Ceramic

Dielectric Relaxations And Formation Mechanism Of Giant Dielectric Constant Step In Cacu3ti4o12 Ceramics

Microstructure-dependent Giant Dielectric Response in CaCu3Ti4O12 Ceramics

Raman and Dielectric Spectra of Cacu3ti3.9o12 Ceramics

Effect of Oxygen Content on Giant Dielectric Constant and Dielectric Process in Cacu3ti4o12

Grain-boundary and subgrain-boundary effects on the dielectric properties of CaCu<sub>3</sub>Ti<sub>4</sub>O<sub>12</sub> ceramics

Decrease of Dielectric Loss in Giant Dielectric Constant CaCu3 Ti4 O12 Ceramics by Adding CaTiO3

Charge transfer in the high dielectric constant materials CaCu3Ti4O12 and CdCu3Ti4O12

Broadband dielectric spectroscopy on single-crystalline and ceramic CaCu3Ti4O12

Dielectric and Impedance Performances of Giant Dielectric Constant Oxide Cacu3ti4o12

Dielectric Properties of Pure and Mn-doped CaCu3Ti4O12 Ceramics over a Wide Temperature Range

Electrical Resistance Transition of CaCu3Ti4O12 Ceramics Induced by Cyclic Voltammetry Conditioning

Structure and Dielectric Relaxation of Double-Perovskite La2cutio6 Ceramics

Structure and modified giant dielectric response in CaCu3(Ti1−xSnx)4O12 ceramics

A novel route to lower the dielectric loss in CaCu$_{3}$Ti$_{4}$O$_{12}$ ceramics

Observation of giant dielectric constant in CdCu3Ti4O12 ceramics

Investigation Of Size Effect On The Giant Dielectric Cacu3ti4o12 Ceramic