Abstract:Ceramic-coated graphite powders are considered as effective raw materials to fabricate three-dimensional continuous ceramic skeleton-reinforced graphite matrix composites which can overcome their inherent poor densification and improve their mechanical and antioxidation properties. However, the morphology and thickness regulation of ceramic coatings on graphite particles are still a great challenge. Herein, SiC-coated graphite (graphite@SiC) powders were prepared by nitriding combustion synthesis using Si and graphited mesocarbon microbead (MCMB) as raw powders with polytetrafluoroethylene (PTFE) as a promoter. The effects of the PTFE content and the Si/MCMB molar ratio on the phase composition and coating morphology were investigated. The phase transition and microstructure evolution of a combustion synthesis (CS) process were revealed by a gas-released quenching experiment. When the Si/MCMB molar ratio was 1 : 3 and the PTFE content was 10 wt%, the thickness of the SiC coating synthesized under 2 MPa N2 reached 1.14 μm. The corresponding sintered graphite@SiC composite had relative density of 99.2% and flexural strength of 231 MPa, accompanied by a significant improvement in high-temperature antioxidation properties. The as-synthesized graphite@SiC powders with good sinterability and antioxidation properties show great promise for applications in the nuclear industry and other extreme fields.

Distribution of Nano-TiN Particles in SiC Ceramic Analysed by SEM/EDS

Preparation and Properties of Nano-Sic-Based Ceramic Composites Containing Nano-Tin

Microstructure And Mechanical Properties Of Sic Ceramic Toughened With Tin Nanoparticles

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Sintering Behavior, Microstructure and Mechanical Properties of Silicon Carbide Ceramics Containing Different Nano-Tin Additive

Analysis on the phase distribution of nano SiC particles coated with Cu

SYNTHESIS AND CHARACTERIZATION OF NANO SiO_2/TiO_(2-x)N_x COMPOSITE PARTICLE

PREPARATION OF TiC/SiC AND TiN/SiC COMPOSITE CERAMICS FROM LIQUID SILICON INFILTRATION

Influence of Conductive Nano-Tic on Microstructural Evolution of Si3n4-Based Nanocomposites in Spark Plasma Sintering

Preparation and sintering behaviour of nanostructured alumina/titania composite powders modified with nano-dopants

Chemical and Wetting Analysis of the Ni-Ti Coating on SiC Improved by a 2-Step Coating-Sintering Process

Preparation and Characterization of Si3n4/Tin Nanocomposites Ceramic Tool Materials

Study on the Ti-C/nano-ceramic additives reaction due to sintering of elemental powders

Investigation on Microstructure and Properties of the Electrodeposited Ni-SiC Composite Coating

Preparation and Magnetic Properties of Nano-nickel Coated Silicon Nitride Composite Powders

PRESSURELESS SINTERING OF SILICON CARBIDE NANOCOMPOSITE CERAMICS

Improving the Microstructure of Si3N4-TiN Composites Using Ammonium Citrate to Disperse Raw TiO2 Powders

Effect of Nano-Si3n4 Addition on the Microstructure and Mechanical Properties of Ticn-Based Cermets

Spark plasma sintering of TiN ceramics codoped with SiC and CNT

Preparation of Pure Nano-Grained Si2N2O Ceramic

Preparation of SiC Coated Graphite Composite Powders by Nitriding Combustion Synthesis