Abstract:This paper assessed the growth of CVD composite coatings on three kinds of cermets and the subsequent high-temperature frictional properties. The carbon to nitrogen ratios (C: N) of Ti(C1-x, Nx) powders added to these three cermets were 5:5,7:3 and 10:0, respectively. It was prepared by powder metallurgy. The TiN/α-Al2O3/Ti(C, N)/TiN multilayer coatings were deposited on different Ti(C, N)-based cermets. The results showed that the crystallinity of the composite coating was affected by the contents of nitrogen content. The inner layer TiN coating exhibited a nano-columnar crystal structure, which detected (111) and (200) orientation texture by XRD. The α-Al2O3 coating and Ti(C, N) coating of the three specimens were coarse columnar crystal structures. The variation in the nitrogen content led to the different performances of the coating. Meanwhile, The CVD coating with a C/N ratio of 7:3 had the best comprehensive properties, because the substrate had similar grain-forming directions and more shape nucleation points. The Electron Backscattered Diffraction (EDSB)、Scanning Electron Microscope (SEM) and Energy Dispersive Spectrometer (EDS) were used to further analyze the microstructure of the samples. The Coating Al2O3 displayed excellent mud (100) value, which indicated that the preferred texture (100) existed and improved the performance of the Al2O3 coating. The adhesion strength of the composite coating on Ti(C0.7, N0.3)-based cermets is the highest. The high-temperature friction wear of the coating was further investigated. Group Y2, which expressed the sample of Ti(C0.7, N0.3)-based cermets CVD coating, demonstrated the lowest wear rate. All control groups’ wear mechanisms included abrasive wear, diffusion wear, and oxidation wear.

Chemical and Wetting Analysis of the Ni-Ti Coating on SiC Improved by a 2-Step Coating-Sintering Process

Mechanism of Ag-SiO2-TiO2 Nanocomposite Coating Formation on NiTi Substrate for Enhanced Functionalization

Investigation on Microstructure and Properties of the Electrodeposited Ni-SiC Composite Coating

Wetting Behaviors of Nickel-Based Alloys on Sintered Silicon Carbide Ceramics

Microstructure, Mechanical, and Tribological Properties of Cr-Ti-Si-N Coatings

EFFECT OF THE N2/Ar FLOW RATIO ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF TiSiCN COATINGS

Wetting and Interfacial Behavior of Molten Al on Mo-Ni(Co)-Si Coated SiC Ceramic

Effect of SiC Contents on Wear Resistance Performance of Electro-Codeposited Ni-SiC Composite Coatings

Effect of Nano-Sized TiN Additions on the Electrical Properties of Vacuum Cold Sprayed SiC Coatings

Effect of SiC Nanoparticles on the Structure and Properties of Ni+W-SiC Nanocoatings

Influence of Si content on structure and mechanical properties of TiAlSiN coatings deposited by multi-plasma immersion ion implantation and deposition

Microstructure evolution, mechanical and abrasive wear properties of NiCrSiB-SiC composite coatings prepared on 16Mn low-carbon steel by Ni-based alloy catalyzed SiC decomposition

The interfacial stability of the coated-SiC/Fe couple

Wettability and Spreading Behavior of Sn–Ti Alloys on Si3N4

Study on Tungsten Metallization and Interfacial Bonding of Silicon Nitride High-Temperature Co-Fired Ceramic Substrates

Study on the growth and wear characters of CVD coating deposited on Ti(C, N)-based cermets with adding different C/N ratios of Ti(C, N) powders

Effect of Α-Al2o3 Coatings on the Interface of Ni/SiC Composites Prepared by Electrodeposition

A Morphological Study and Effect of Intermediate Phase Formation on Hard and Wear Resistant SiC-Co Composite Coating on Low Carbon Steel via Arc Based Heat Source

Study on Interface Microstructure and Laser Re-melting NiCrBSi+TiN Coating

Preparation, mechanical properties and wear resistance of dual-sized TiC particles reinforced high-entropy alloy cermet coating

Fabrication of Ni60–SiC Coating on Carbon Steel for Improving Friction, Corrosion Properties