Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

In-situ synthesis of WC–Co composite powder and densification by sinter-HIP

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Synthesis of ultrafine WC-10Co composite powders with carbon boat added and densification by sinter-HIP

Ultra-fine Grain Cemented Carbide Fabricated from WC-Co Composite Powder by In-situ Synthesis

Synthesis of WC-Co Composite Powder by Reduction and Carbonization Reactions and Its Densification

Synthesis and characterization of WC-Co nanosized composite powders with in situ carbon and gas carbon sources

Preparation of Ultrafine WC-10Co Composite Powders by Reduction and Carbonization

Synthesis of Ultrafine WC-Co Core-shell Composite Powders by Chemical Reduction Method

A Novel Route for the Synthesis of Ultrafine WC-15wt %co Cemented Carbides

Synthesis Of Ultrafine Wc-Co Composite Powders Under Hydrogen Atmosphere With Insitu Carbon Via A One-Step Reduction-Carbonization Process

WC Strengthened W–Cu Nanocomposite Powder Synthesized by In-Situ Reactions

Synthesis of WC Composite Powder with Nano-Cobalt Coatings and Its Application in WC-4Co Cemented Carbide

Synthesis and Characterization of WC-6Co Nanocrystalline Composite Powder

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method

A short and facile process to synthesize WC-Co cemented carbides

Effects of ultrafine WC on the densification behavior and microstructural evolution of coarse-grained WC-5Co cemented carbides

In-situ synthesis of core-shell structure W(WC) composite grains in W-Cu composites fabricated by infiltration

Preparation and Sintering of WC–Co Composite Powders for Coarse Grained WC–8Co Hardmetals

Preparation and characterization of high-performance in-situ synthesized WC reinforced nickel-based coatings

Synthesis of WC-Co Composite Powders with Two-Step Carbonization and Sintering Performance Study