Lithium Ion Conductivity of the B-site Substitution in Li 3x La 0.67−x RE Y III Ti 1−2y P Y O 3 System (RE III =sc 3+ , Y 3+ , Nd 3+ , Sm 3+ , Eu 3+ , Yb 3+ )

Ronghua Li,Liyun Zi,Chunzhi Shen,Wenji Wang

DOI: https://doi.org/10.1007/bf02430414

IF: 2.961

2005-01-01

Ionics

Abstract:The B-site substituted perovskite solid solution systems Li 3x La 0.67−x RE y Ti 1−2y P y O 3 (RE=Sc, Y, Nd, Sm, Eu, Yb) have been investigated. Perovskite solid solutions formed in the range of x=0.10, y<0.10 for RE=Sc 3+ , Y 3+ , Yb 3+ , x=0.10, y≤0.05 for RE=Nd 3+ , Sm 3+ , Eu 3+ . Li 0.3 La 0.57 Nd 0.05 Ti 0.9 P 0.05 O 3 has the highest bulk conductivity of 4.31×10 −4 S·cm −1 and the highest total conductivity of 2.52×10 −4 S·cm −1 at room temperature in all prepared compositions. The compositions have low activation energies of about 24–30 kJ/mol in the temperature ranges of 298–523 K. SEM studies showed that the sample made by solid-state reaction has a sphere-like morphology and a rough particle with particle size of about 50 µm. The research results also indicated that the reaction temperature decreases and the electrochemical stabilities of the titanate-based perovskite-type solid solutions are improved by using RE 3+ and P 5+ replaced Ti 4+ on B-site in the Li 3x La 0.67−x TiO 3 parent.