Abstract:Three series of porous carbon fibers were prepared by electrochemical oxidation of a synthetic polyacrylonitrile-based fiber to various degrees. The electrooxidized fibers were characterized by N2 adsorption at 77K, CO2 adsorption at 273K, NaOH neutralization and X-ray photoelectron spectroscopy (XPS). In all cases standard BET surface areas calculated from nitrogen adsorption data barely exceeded the geometric area of the fiber itself (ca 1m2g−1). In contrast, surface areas derived by applying the Dubinin–Radushkevich (DR) method to CO2 adsorption data increased fairly linearly from ca 1 to 132m2g−1 with increasing electrooxidation severity. NaOH uptakes were also found to increase linearly as a function of electrooxidation severity. It is thus inferred that: (1) N2 adsorption at 77K is severely hindered because of activated N2 diffusion effects; and (2) by virtue of their thinner dimension and faster diffusion rate at 273K, CO2 molecules manage to probe the entire pore structure of the carbon fibers. Therefore, a new model based on density functional theory (DFT) was applied to CO2 adsorption data at 273K in order to generate true pore size distributions (PSDs) of the fibers tested. The DFT/CO2 method revealed that the PSDs of the electrooxidized fibers are neither Gaussian nor monomodal. Comparison with steam activated synthetic and natural plant (Kenaf) fibers revealed that ultramicroporous fibers possess PSD peaks at ca 0.4, 0.6, 0.8 and 1.1nm. The peak at ca 0.4 was dominant and negligible when the DR/CO2 to BET/N2 surface area ratios were >1 and <1, respectively. It is therefore concluded that pores of ca 0.4nm width are responsible for activated N2 diffusion at 77K.

Pore structure and fractal characteristics of activated carbon fibers characterized by using HRTEM

THE RESEARCH ON TRACTAL OF ACTIATED CARBON FIBER BY NITROGEN ADSORPTION

FRACTAL THEORY AND APPLICATION IN ACTIVATED CARBONS

Study of Microstructure of High-Surface-Area Polyacrylonitrile Activated Carbon Fibers.

Adsorption and Porous Structure of High-Surface Area PAN-ACF

Pore Structures and Adsorption Properties of Fluorinated Activated Carbon Fiber

Carbon Dioxide Adsorption on Carbon Nanofibers with Different Porous Structures

Hierarchical Pore Structure of Activated Carbon Fabricated by CO2/microwave for Volatile Organic Compounds Adsorption

Adsorption of Volatile Organic Compounds on Activated Carbon Fiber Prepared by Carbon Dioxide

Surface area and pore size distribution of microporous carbon fibers prepared by electrochemical oxidation

Research on Surface Properties of Modified Activated Carbon Fiber and Its Mercury Adsorption Performance

Preparation and hydrogen storage of activated rayon-based carbon fibers with high specific surface area

Pore structure effects on activated carbon adsorption behavior for toluene

Fractal Analysis of Pore Structure of Eucalyptus Pulp Fibers

A comparative analysis of polyacrylonitrile-based carbon fibers: (I) Microstructures

Fractal carbon nanotube fibers with mesoporous crystalline structure

Comparative studies of porous carbon nanofibers by various activation methods

Influence of Carbonification Condition on Carbon Fiber Nanometer Micropore Fractal Dimension

Effect of Carbonization Temperature on Microstructure of PAN-based Activated Carbon Fibers Prepared by CO2 Activation

PVA-based Activated Carbon Fibers with Lotus Root-Like Axially Porous Structure

Adsorption Models and Structural Characterization for Activated Carbon Fibers