Abstract:Three series of porous carbon fibers were prepared by electrochemical oxidation of a synthetic polyacrylonitrile-based fiber to various degrees. The electrooxidized fibers were characterized by N2 adsorption at 77K, CO2 adsorption at 273K, NaOH neutralization and X-ray photoelectron spectroscopy (XPS). In all cases standard BET surface areas calculated from nitrogen adsorption data barely exceeded the geometric area of the fiber itself (ca 1m2g−1). In contrast, surface areas derived by applying the Dubinin–Radushkevich (DR) method to CO2 adsorption data increased fairly linearly from ca 1 to 132m2g−1 with increasing electrooxidation severity. NaOH uptakes were also found to increase linearly as a function of electrooxidation severity. It is thus inferred that: (1) N2 adsorption at 77K is severely hindered because of activated N2 diffusion effects; and (2) by virtue of their thinner dimension and faster diffusion rate at 273K, CO2 molecules manage to probe the entire pore structure of the carbon fibers. Therefore, a new model based on density functional theory (DFT) was applied to CO2 adsorption data at 273K in order to generate true pore size distributions (PSDs) of the fibers tested. The DFT/CO2 method revealed that the PSDs of the electrooxidized fibers are neither Gaussian nor monomodal. Comparison with steam activated synthetic and natural plant (Kenaf) fibers revealed that ultramicroporous fibers possess PSD peaks at ca 0.4, 0.6, 0.8 and 1.1nm. The peak at ca 0.4 was dominant and negligible when the DR/CO2 to BET/N2 surface area ratios were >1 and <1, respectively. It is therefore concluded that pores of ca 0.4nm width are responsible for activated N2 diffusion at 77K.

THE RESEARCH ON TRACTAL OF ACTIATED CARBON FIBER BY NITROGEN ADSORPTION

Pore structure and fractal characteristics of activated carbon fibers characterized by using HRTEM

Adsorption of Volatile Organic Compounds on Activated Carbon Fiber Prepared by Carbon Dioxide

Research on Surface Properties of Modified Activated Carbon Fiber and Its Mercury Adsorption Performance

Adsorption characteristics of trace volatile organic compounds on activated carbon fibres at room temperature

Adsorption Of Volatile Organic Compounds In Nitrogen Streams On Oxidized Activated Carbon Fibres

Effect of Oxidation Treatment on Surface Fractal Dimension of Activated Carbon Fiber

Correlation of Fractal Pore-Size Distribution of Activated Carbon Fiber with Its Adsorption for Low Concentration Benzene Vapor

Adsorption of trace polar methy-ethyl-ketone and non-polar benzene vapors on viscose rayon-based activated carbon fibers

Porous carbon fibers from low-temperature sodium amide activation for acetone adsorption

Carbon Dioxide Adsorption on Carbon Nanofibers with Different Porous Structures

Preparation and hydrogen storage of activated rayon-based carbon fibers with high specific surface area

Adsorption Characteristics of Carbon Tetrachloride from Aqueous Solution Onto Polyacrylonitrile-Based Activated Carbon Fiber

The surface fractal investigation on carbon nanotubes modified by the adsorption of poly(acrylic acid)

Effect of Temperature on the Adsorption of Organic Vapours on Activated Carbon Fibres

Investigation on the surface properties of the carbon nanotubes before and after the adsorption of polyacrylic acid

Comparative studies of porous carbon nanofibers by various activation methods

Study on adsorption performance of polyacrylonitrile-based activated carbon fiber for trace of hexavalent chromium

Adsorption of benzene and ethanol on activated carbon nanofibers prepared by electrospinning

Adsorption Property, Kinetic and Equilibrium Studies of Activated Carbon Fiber Prepared from Liquefied Wood by Zncl2 Activation

Surface area and pore size distribution of microporous carbon fibers prepared by electrochemical oxidation