Abstract:Activated carbon (AC) fiber is a carbonaceous material with a porous structure that has a tremendous scope of application in different fields. Conventionally, AC is derived from fossil fuel-based raw materials like polyacrylonitrile (PAN) and pitch. In this work, AC was synthesized from eco-friendly, renewable, and ubiquitous jute fiber. Systematically, the jute fiber was washed and pretreated with NaOH. Raw jute and NaOH-treated jute were carbonized/pyrolyzed at 500 °C for 1 h in presence of N2 gas. The carbonized carbon was activated with H3PO4 and KOH and again pyrolyzed at 650 °C for 1.5 h maintaining the inert condition. The different features of activated carbons were characterized with field emission-scanning electron microscope, energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray diffraction (XRD), and thermogravimetric analysis. The average yield of carbonized and activated carbons was recorded at 19 and 13.8%, respectively. The scanning electron microscopic images confirmed a honeycomb-like porous structure. It was observed that KOH-activated carbon exhibited a more porous structure than the H3PO4-activated carbons. The average pore diameter of activated carbons was noted to be 1.3 μm. The pore density was higher in case of KOH-activated carbons accounting for 2.15 pore/μm. The EDX analysis showed that H3PO4-activated carbons had more than 90% carbon atoms indicating a significant carbon content. The TEM images revealed that AC particles were in the nanoscale range. The average particle sizes of H3PO4-activated carbon and KOH-activated carbon were 36.38 and 32.8 nm, respectively. The XRD study demonstrated the highly disordered and low level of crystallinity of AC. It was detected that the AC showed much higher thermal resistance than the jute fiber. The H3PO4-activated carbon obtained from NaOH-treated jute remained at 84% even after 500 °C. A higher thermal resistance was achieved with H3PO4-activated carbon since it contains 0.56% phosphorus, which was confirmed by EDX investigation. It was found that a higher carbon yield was obtained from NaOH-treated jute. The porous structure of the material showed that it could be used as an adsorbent. Due to its high thermal stability, it is recommended for flame retardants and heat insulation applications as well.

Comparative studies of porous carbon nanofibers by various activation methods

Optimal Activation of Porous Carbon for High Performance CO2 Capture

Carbon Dioxide Adsorption on Carbon Nanofibers with Different Porous Structures

Preparation of porous carbons from phenol–formaldehyde resins with chemical and physical activation

Effect of Porosity and Crystallinity of Activated Carbons for Electrochemical Capacitors

Numerical Analysis of the Porous Structure of Activated Carbons Derived from Synthetic Polymers

Mechanism of Biomass Activation and Ammonia Modification for Nitrogen-Doped Porous Carbon Materials.

Chemical Activation Characteristics of Pitch-Based Carbon Fibers by KOH

Mathematical analysis of the effect of process conditions on the porous structure development of activated carbons derived from Pine cones

Preparation of High-Surface-Area Activated Carbon from Coconut Shell Fibers

Synthesis, Activation, and Characterization of Carbon Fiber Precursor Derived from Jute Fiber

Hierarchical Pore Structure of Activated Carbon Fabricated by CO2/microwave for Volatile Organic Compounds Adsorption

Preparation and Characterization of Activated Carbons Based Alkali Lignin by KOH Chemical Activation

Characterization and analysis of activated carbons prepared from furfural residues by microwave-assisted pyrolysis and activation

Preparation and hydrogen storage of activated rayon-based carbon fibers with high specific surface area

Optimization of the Preparation Conditions of KOH-activated, PAN-based Carbon Ellipsoids by Orthogonal Experimental Analysis

ACF PORE STRUCTURE FOR ACTIVATION KOH AND CO_2

Porous carbon fibers from low-temperature sodium amide activation for acetone adsorption

Investigating the effects of activating agent morphology on the porosity and related capacitance of nanoporous carbons

Post-treatment strategies for pyrophoric KOH-activated carbon nanofibres

Preparation and characterization of polyacrylonitrile-based activated carbon nanofibers/graphene (gACNFs) composite synthesized by electrospinning