Abstract:The concept of grain boundary engineering (GBE) has been proposed based on the fact that many studies have demonstrated that boundaries associated with low Sigma-value coincident site lattice (CSL) misorientations show higher resistance to intergranular fracture and corrosion, reduced susceptibility to impurity segregation and superior ductility. It is commonly accepted that for fcc metals of low to medium stacking fault energy metals, including Ni and many Ni-alloys, the most important CSL boundary for the GBE process is a Sigma 3 boundary, the occurrence of which is dominated by the formation of annealing twins. Moreover, it has been found that repetitive thermo-mechanical processing can be used to increase further the fraction of Sigma 3 (and Sigma 3(n) (n >1)) boundaries. However, the mechanism for this is not yet clear. Therefore, an investigation on the evolution of Sigma 3 boundaries during recrystallization is important for understanding the mechanisms of GBE for those materials. In the present paper the evolution of Sigma 3 boundaries during recrystallization in a 96% cold-rolled sample of pure nickel of 99.996% purity has been explored using orientation maps obtained using electron backscatter diffraction (EBSD). Each orientation map was taken from the same area after annealing for various times. Based on the EBSD data the Sigma 3 boundaries can be divided into two groups: "twin" type and "non-twin" type. These groups can be differentiated using a parameter of deviation angle (Delta theta) of boundary misorientation to the ideal twin misorientation (60 degrees < 111 >). During recrystallization incoherent twin boundaries are found to develop from coherent twin boundaries. It is also that most Sigma 3(n) (n >1) boundaries are formed by impringement of a nucleus with its n-order twins, and that the chance for such impingement events decreases significantly with increasing n. Most non-twin type Sigma 3 boundaries arise from impingement of Sigma 1 and twin type Sigma 3 boundaries. Non-twin type Sigma 3 boundaries may be more effective than twin type Sigma 3 boundaries to develop a beneficial grain boundary network.

The Orientations of Nuclei at Triple Junctions in Deformed Columnar Grain Ni

Evolution of Orientations and Deformation Structures Within Individual Grains in Cold Rolled Columnar Grained Nickel

Deformation And Annealing Textures Of Extruded And Cold Rolled Pure Ni Single Crystals Of Cube Orientation

Systematical Analysis on the Grain Orientation Evolution of Pure Nickel under Plastic Deformation by Using In-Situ EBSD

Recovery and Recrystallization as a Function of Deformed Microstructure Orientation in Coarse Grained Cold-Rolled Ni

Orientation-Dependent Characteristics for Residual Grains During Hot Deformation of Nickel-Based Alloy 925

Experimental Observation and Modelling of the Orientation Evolution of Individual Grains in Columnar Grain Ni During Cold Rolling

Orientations of Nuclei During Static Recrystallization in a Cold-Rolled Mg-Zn-Gd Alloy

Investigation of Boundary Migration During Grain Growth in Fully Recrystallised High Purity Nickel

Texture and Deformation Structure Evolution During Rolling of Individual Grains of Columnar Grain Nickel

Origin of Recrystallized Cubic Orientation Grains in Face-Centered Cubic Metals

Investigation of the Microstructure and Rolling Texture Evolution of Cu-45 At.% Ni Alloys During the Recovery Process by Quasi-In Situ Electron Backscatter Diffraction

Microstructure–grain Orientation Relationship in Coarse Grain Nickel Cold-Rolled to Large Strain

The effect of grain boundary structures on crack nucleation in nickel nanolaminated structure: A molecular dynamics study

Grain Orientation Induced Softening in Electrodeposited Gradient Nanostructured Nickel during Cold Rolling Deformation

Evolution of Sigma 3 Boundaries During Recrystallization of Cold-Rolled Nickel Deformed to High Strain

Deformation Strain Inhomogeneity in Columnar Grain Nickel

Development of the Cube Texture at Low Annealing Temperatures in Highly Rolled Pure Nickel

A study on the orientation inheritance in laminated NiAl produced by in situ reaction annealing

Analysis of the Growth of Individual Grains During Recrystallization in Pure Nickel

MICROSTRUCTURAL EVOLUTION OF COLUMNAR GRAIN Al DURING COLD ROLLING II. Mircoscopic Subdivision