Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

INITIATION AND PROPAGATION BEHAVIOR OF A FATIGUE CRACK OF ALLOY 718

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Fatigue crack propagation behavior of IN718 superalloy aged with temperature/stress coupled field

Fatigue behavior and fracture characteristics of 718Plus nickel-based superalloy at high temperature

Analysis of Microporosity-Dependent Fatigue Crack Behavior in Alloy 718 by Using Synchronic Radiation X-Ray CT and FEM

Fracture Mechanisms Induced by Microporosity and Precipitates in Isothermal Fatigue of Polycrystalline Nickel Based Superalloy

Computational Analysis of Fatigue Crack Propagation at Elevated Temperature for In718

Crack Initiation Mechanism in a High-Strength Ti-5Al-7.5V Alloy Subjected to High Cycle Fatigue Loading

The study of 650 degrees C low cycle fatigue properties on alloy 718 DA turbine disk

Multi-scale Study of Subsurface Fatigue Cracking Behavior of Laser-Powder Bed Fused Inconel 718 at Stress Ratios and Temperatures

Fatigue Crack-Initiation Mechanisms of a Dual-Phase Titanium Alloy Exhibiting High Tensile and High-Cycle Fatigue Properties

Fatigue crack nucleation behavior in nickel-based PM alloy

On the Microstructure Evolution During Low Cycle Fatigue Deformation of Wrought ATI 718plus Alloy

The Mechanism of Creep during Crack Propagation of a Superalloy under Fatigue–Creep–Environment Interactions

Influence of orientation and temperature on the fatigue crack growth of a nickel-based directionally solidified superalloy

The Numerical Simulation of Fatigue Crack Propagation in Inconel 718 Alloy at Different Temperatures

Fatigue and Fracture Behavior of Nickel-Based Superalloy Inconel 718 Up to the Very High Cycle Regime

Study of Fatigue Crack Initiation and the Propagation Mechanism Induced by Pores in a Powder Metallurgy Nickel-Based FGH96 Superalloy

Effect of Solution Aging Treatment on High and Very High Cycle Fatigue Properties of Nickel-Based Alloy Fabricated by Laser Powder Bed Fusion at 25 °C and 650 °C

An Experimental Methodology for Quantitative Characterization of Multi-Site Fatigue Crack Nucleation in High-Strength Al Alloys

Mechanism of Precipitate Microstructure Affecting Fatigue Behavior of 7020 Aluminum Alloy