Abstract:In this study , a dual-scale numerical procedure is developed to reveal the creep-fatigue damage mechanisms and estimate the crack initiation life for notched structures made of Inconel 718 superalloy at 650°C. The macro-scale simulation solves the creep-fatigue deformation behavior with viscoplastic constitutive models, and the local deformation histories are supplied to the micro-scale simulation as boundary conditions. In the micro-scale simulation, the local damage evolutions are solved based on crystal plasticity combined with grain boundary cavity model. The creep damage is calculated by a special formulation in the form of cavity nucleation, growth and coalescence. The fatigue damage is represented by accumulated energy dissipation originated from crystal plasticity finite element simulation. Experimentally, the creep-fatigue tests of notched structures are carried out for Inconel 718 superalloy at 650°C to validate the feasibility and robustness of the proposed numerical procedure. Moreover, the crack initiation behavior, including transgranular cracks under fatigue loading and intergranular cracks under creep-fatigue loading, is explained through different types of microstructure observations together with a dual-scale numerical procedure. In detail, the crack initiation sites transferred from the grain interior at notched surface to the grain boundaries at notched subsurface with an increase in hold times can be well predicted by the proposed numerical procedure. In addition, the simulated life based on the developed life prediction approach agrees well with the experimental data within an error band of ±2. Parametric studies show that the creep damage is more sensitive to grain boundary diffusion than to the external conditions of strain level and hold time.

Computational Analysis of Fatigue Crack Propagation at Elevated Temperature for In718

Numerical Simulation of Creep-Fatigue Crack Growth for Nickel-Based Super Alloy with Extended Finite Element Method

Study on Creep Behavior and Fracture Life Prediction Method of P92 Steel Based on Finite Element Analysis

Creep‐fatigue Deformation Characteristics and Life Prediction Model of Inconel 718 Superalloy under Hybrid Stress–strain‐controlled Mode

Creep-fatigue damage mechanisms and life prediction based on crystal plasticity combined with grain boundary cavity model in a nickel-based superalloy at 650°C

A Concise Binomial Model for Nonlinear Creep-Fatigue Crack Growth Behavior at Elevated Temperatures

The Mechanism of Creep during Crack Propagation of a Superalloy under Fatigue–Creep–Environment Interactions

A crystal plasticity-based approach for creep-fatigue life prediction and damage evaluation in a nickel-based superalloy

Fatigue crack propagation behavior of IN718 superalloy aged with temperature/stress coupled field

Application of a Cohesive Zone Model for Simulating Fatigue Crack Growth from Moderate to High <mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" id="M1"><mml:mi mathvariant="normal">Δ</mml:mi><mml:mi>K</mml:mi></mml:math> Levels of Inconel 718

Fatigue behavior and fracture characteristics of 718Plus nickel-based superalloy at high temperature

Studies of High-Temperature Fatigue Behavior and Mechanism for Nickel-Based Superalloy Inconel 625

Application Of A Cohesive Zone Model For Simulating Fatigue Crack Growth From Moderate To High Delta K Levels Of Inconel 718

Cycle-dependent creep-fatigue deformation and life predictions in a nickel-based superalloy at elevated temperature

Creep-fatigue life prediction in nickel-based superalloy GH4169 based on microstructural damage quantification with the help of electron backscatter diffraction

Fatigue and Fracture Behavior of Nickel-Based Superalloy Inconel 718 Up to the Very High Cycle Regime

A combined cyclic viscoplasticity and entropy generation approach for modelling fatigue crack growth behavior of nickel-based superalloy at high temperature

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

A dual-scale modelling approach for creep-fatigue crack initiation life prediction of holed structure in a nickel-based superalloy

A novel very-high-cycle-fatigue life prediction model with interior microstructure induced cracking behavior of Inconel-713C superalloy at 25 °C, 750 °C and 1000 °C

Creep–fatigue Interaction Behavior of Nickel-Based Single Crystal Superalloy at High Temperature by In-Situ SEM Observation