Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

Fatigue and Fracture Behavior of Nickel-Based Superalloy Inconel 718 Up to the Very High Cycle Regime

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Creep‐fatigue Deformation Characteristics and Life Prediction Model of Inconel 718 Superalloy under Hybrid Stress–strain‐controlled Mode

A novel very-high-cycle-fatigue life prediction model with interior microstructure induced cracking behavior of Inconel-713C superalloy at 25 °C, 750 °C and 1000 °C

Fracture Mechanisms Induced by Microporosity and Precipitates in Isothermal Fatigue of Polycrystalline Nickel Based Superalloy

Multi-stage dwell fatigue crack growth behaviors in a nickel-based superalloy at elevated temperature

Fatigue behavior and fracture characteristics of 718Plus nickel-based superalloy at high temperature

Very-High-Cycle-Fatigue Property of IN 718 Manufactured by Selective Laser Melting at Elevated Temperature: Microstructure-Related Failure Behavior and Life Prediction

Studies of High-Temperature Fatigue Behavior and Mechanism for Nickel-Based Superalloy Inconel 625

Failure mechanism and life correlation of Inconel 718 in high and very high cycle fatigue regimes

Creep-fatigue damage mechanisms and life prediction based on crystal plasticity combined with grain boundary cavity model in a nickel-based superalloy at 650°C

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

The Numerical Simulation of Fatigue Crack Propagation in Inconel 718 Alloy at Different Temperatures

Ex-situ observation of the short crack initiation and propagation behaviour of nickel-base wrought alloy Inconel 718 for critical rotating components under fatigue conditions at elevated temperatures

Cyclic microstructure analysis, crack propagation and life prediction of Inconel 750H considering the slip fracture energy

Application of a Cohesive Zone Model for Simulating Fatigue Crack Growth from Moderate to High <mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" id="M1"><mml:mi mathvariant="normal">Δ</mml:mi><mml:mi>K</mml:mi></mml:math> Levels of Inconel 718

Computational Analysis of Fatigue Crack Propagation at Elevated Temperature for In718

High‐cycle and very‐high‐cycle fatigue behavior and life prediction of Ni‐based superalloy at elevated temperature

A unified material model for multiaxial ductile fracture and extremely low cycle fatigue of Inconel 718

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser