Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Failure mechanism and life correlation of Inconel 718 in high and very high cycle fatigue regimes

Creep‐fatigue Deformation Characteristics and Life Prediction Model of Inconel 718 Superalloy under Hybrid Stress–strain‐controlled Mode

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Fatigue and Fracture Behavior of Nickel-Based Superalloy Inconel 718 Up to the Very High Cycle Regime

Comparison of the Very High Cycle Fatigue Behaviors of INCONEL 718 with Different Loading Frequencies

In-situ SEM-EBSD investigation of the low-cycle fatigue deformation behavior of Inconel 718 at grain-scale

Application of a Cohesive Zone Model for Simulating Fatigue Crack Growth from Moderate to High <mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" id="M1"><mml:mi mathvariant="normal">Δ</mml:mi><mml:mi>K</mml:mi></mml:math> Levels of Inconel 718

A unified material model for multiaxial ductile fracture and extremely low cycle fatigue of Inconel 718

Fatigue behavior and fracture characteristics of 718Plus nickel-based superalloy at high temperature

Cyclic microstructure analysis, crack propagation and life prediction of Inconel 750H considering the slip fracture energy

A novel very-high-cycle-fatigue life prediction model with interior microstructure induced cracking behavior of Inconel-713C superalloy at 25 °C, 750 °C and 1000 °C

Role of defects and microstructure on the fatigue durability of Inconel 718 obtained by additive layer manufacturing route

Very-High-Cycle Fatigue Behavior of Inconel 718 Alloy Fabricated by Selective Laser Melting at Elevated Temperature

Application Of A Cohesive Zone Model For Simulating Fatigue Crack Growth From Moderate To High Delta K Levels Of Inconel 718

Cyclic response and residual life prediction of Inconel 718 superalloy after overloading under hybrid stress-strain controlled creep-fatigue loading

Experimental and Modeling Study on Small Fatigue Crack Initiation and Propagation Behavior of Inconel 617

Multi-stage dwell fatigue crack growth behaviors in a nickel-based superalloy at elevated temperature

Crack initiation mechanisms and life prediction of GH4169 superalloy in the high cycle and very high cycle fatigue regime

Influence of Heat Treatment on Cyclic Response of Nickel-Based Superalloy Inconel 718 up to Very-High Cycle Regime

Very High Cycle Fatigue Failure Analysis and Life Prediction of Cr-Ni-W Gear Steel Based on Crack Initiation and Growth Behaviors

Investigation of the fatigue damage mechanism of Inconel 617 at elevated temperatures obtained by in situ SEM fatigue tests