Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Comparison of the Very High Cycle Fatigue Behaviors of INCONEL 718 with Different Loading Frequencies

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Failure mechanism and life correlation of Inconel 718 in high and very high cycle fatigue regimes

Fatigue and Fracture Behavior of Nickel-Based Superalloy Inconel 718 Up to the Very High Cycle Regime

Fatigue behavior and fracture characteristics of 718Plus nickel-based superalloy at high temperature

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Influence of Heat Treatment on Cyclic Response of Nickel-Based Superalloy Inconel 718 up to Very-High Cycle Regime

Very-High-Cycle-Fatigue Property of IN 718 Manufactured by Selective Laser Melting at Elevated Temperature: Microstructure-Related Failure Behavior and Life Prediction

Creep‐fatigue Deformation Characteristics and Life Prediction Model of Inconel 718 Superalloy under Hybrid Stress–strain‐controlled Mode

Influence of the Loading Frequency on Very High Cycle Fatigue Behavior of Structural Steels

Very-High-Cycle Fatigue Behavior of Inconel 718 Alloy Fabricated by Selective Laser Melting at Elevated Temperature

Studies of High-Temperature Fatigue Behavior and Mechanism for Nickel-Based Superalloy Inconel 625

Fracture Mechanisms Induced by Microporosity and Precipitates in Isothermal Fatigue of Polycrystalline Nickel Based Superalloy

Multi-stage dwell fatigue crack growth behaviors in a nickel-based superalloy at elevated temperature

Very high cycle fatigue of a notched Ni-based single crystal superalloy at high temperature

The Numerical Simulation of Fatigue Crack Propagation in Inconel 718 Alloy at Different Temperatures

Effects of hydrogen and load frequency on the fatigue crack propagation behavior of selective laser melted Inconel 718 alloy

Analysis of the crack initiation and short crack propagation of laser cladding IN718 enduring fretting fatigue at 650 °C

A study of high cycle fatigue life and its correlation with microstructural parameters in IN713C nickel-based superalloy

The Effects of Inhomogeneous Microstructure and Loading Waveform on Creep-Fatigue Behaviour in a Forged and Precipitation Hardened Nickel-Based Superalloy

Fatigue crack propagation behavior of IN718 superalloy aged with temperature/stress coupled field