Abstract:This study provides a thorough analysis of the fatigue resistance of two low-alloy ultrahigh-strength steels (UHSSs): Steel A (fully martensitic) and Steel B (martensitic–bainitic). The investigation focused on the fatigue behaviour, damage mechanisms, and failure modes across different microstructures. Fatigue strength was determined through fully reversed tension–compression stress-controlled fatigue tests. Microstructural evolution, fracture surface characteristics, and crack-initiation mechanisms were investigated using laser scanning confocal microscopy and scanning electron microscopy. Microindentation hardness (HIT) tests were conducted to examine the cyclic hardening and softening of the steels. The experimental results revealed that Steel A exhibited superior fatigue resistance compared to Steel B, with fatigue limits of 550 and 500 MPa, respectively. Fracture surface analysis identified non-metallic inclusions (NMIs) comprising the complex MnO-SiO2 as critical sites for crack initiation during cyclic loading in both steels. The HIT results after fatigue indicated significant cyclic softening for Steel A, with HIT values decreasing from 7.7 ± 0.36 to 5.66 ± 0.26 GPa. In contrast, Steel B exhibited slight cyclic hardening, with HIT values increasing from 5.24 ± 0.23 to 5.41 ± 0.31 GPa. Furthermore, the martensitic steel demonstrated superior yield and tensile strengths of 1145 and 1870 MPa, respectively. Analysis of the fatigue behaviour revealed the superior fatigue resistance of martensitic steel. The complex morphology and shape of the NMIs, examined using the 3D microstructure characterisation technique, demonstrated their role as stress concentrators, leading to localised plastic deformation and crack initiation.

Influence of the Loading Frequency on Very High Cycle Fatigue Behavior of Structural Steels

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Usability of Ultrasonic Frequency Testing for Rapid Generation of High and Very High Cycle Fatigue Data

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Interpretation of Frequency Effect for High-Strength Steels with Three Different Strength Levels via Crystal Plasticity Finite Element Method

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Ultrasonic Fatigue Testing of Structural Steel S275JR+AR with Insights into Corrosion, Mean Stress and Frequency Effects

Influence of the strain rate on the fatigue behaviour of fully ferritic high chromium steel and P91 steel at high temperatures

Influence of Loading Waveform on the Fatigue Life of 34CrNi3MoVA Steel

Comparative Study of High-Cycle Fatigue and Failure Mechanisms in Ultrahigh-Strength CrNiMoWMnV Low-Alloy Steels

Effect of Cyclic Load Frequency on the Fatigue Crack Nucleation and Growth of Annealed and Prestrained Austenitic SS 304

Comparison of the Very High Cycle Fatigue Behaviors of INCONEL 718 with Different Loading Frequencies

Characterization and Evaluation of a Railway Wheel Steel in the HCF and VHCF Regimes

Experimental and Numerical Study of Combined High and Low Cycle Fatigue Performance of Low Alloy Steel and Engineering Application

Low cycle fatigue and creep-fatigue interaction behavior of 2.25CrMoV steel at high temperature

Effects of stress ratio on the temperature-dependent high-cycle fatigue properties of alloy steels

Low Cycle Fatigue and Damage Evaluation on 16MnCr5 Alloy Steel

Fatigue Strengths of the 54sicr6 Steel under Different Cyclic Loading Conditions

Low-cycle fatigue in ultra-high-strength steel welded joints in the as-welded and post-weld-treated conditions

Influence of time and temperature dependent processes on strain controlled low cycle fatigue behavior of alloy 617