Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Influence of time and temperature dependent processes on strain controlled low cycle fatigue behavior of alloy 617

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Strain Ratio Effects on Low-Cycle Fatigue Behavior and Deformation Microstructure of 2124-T851 Aluminum Alloy

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Effects of temperature on the low cycle fatigue behaviour of nitrogen alloyed type 316L stainless steel

Influence of Prior Low Cycle Fatigue on Microstructure Evolution and Subsequent Creep Behavior

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Effect of stress-hold and strain-hold during Creep-Fatigue Interaction of alloy 617 M

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

Microstructural damage assessment in alloy 617M near high cycle fatigue threshold at elevated temperature

Strain‐Controlled Low‐Cycle Fatigue Behavior of a Superalloy Considering Extensive Temperature Range and Stress Concentration

Low cycle fatigue of a nickel based superalloy at high temperature: deformation microstructures

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

Studies of High-Temperature Fatigue Behavior and Mechanism for Nickel-Based Superalloy Inconel 625

Mechanisms of deformation, damage and life behavior of inconel 617 alloy during creep-fatigue interaction at 700 °C