Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

The study of 650 degrees C low cycle fatigue properties on alloy 718 DA turbine disk

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Very-High-Cycle-Fatigue Property of IN 718 Manufactured by Selective Laser Melting at Elevated Temperature: Microstructure-Related Failure Behavior and Life Prediction

On the Microstructure Evolution During Low Cycle Fatigue Deformation of Wrought ATI 718plus Alloy

Effect of Surface Modification on the High Temperature Low Cycle Fatigue Performance of LPBF 316L Austenitic Steel

Characterization of Low Cycle Fatigue of Ferritic–Martensitic P92 Steel: Effect of Temperature

INITIATION AND PROPAGATION BEHAVIOR OF A FATIGUE CRACK OF ALLOY 718

High Temperature Low Cycle Fatigue Properties and Failure Mechanism of a TiAl Alloy

Influence of time and temperature dependent processes on strain controlled low cycle fatigue behavior of alloy 617

Low cycle fatigue and creep-fatigue behavior of a high temperature alloy on smooth and notched specimens

Study of Low-Cycle Fatigue of AL6XN Austenitic Stainless Steel

Effect of Dwell Condition on Fatigue Behavior of a High-Nb TiAl Alloy at 750 °C

Fatigue behavior and fracture characteristics of 718Plus nickel-based superalloy at high temperature

Effect of Solution Aging Treatment on High and Very High Cycle Fatigue Properties of Nickel-Based Alloy Fabricated by Laser Powder Bed Fusion at 25 °C and 650 °C

Low Cycle Fatigue of 9-12% Cr Steel at Elevated Temperature: Cyclic Deformation Behavior and Life Assessment

Combined high and low cycle fatigue analysis of FGH96 alloy under high temperature conditions

Effect of aging state on low cycle fatigue performance of AA 2099 alloy