Tem Observation of the Al3er Phase During Homogenizing of the 5083 Alloy with Er Addition

Lin Shuangping,Huang Hui,Wen Shengping,Nie Zuoren
DOI: https://doi.org/10.3321/j.issn:0412-1961.2009.08.013
IF: 1.797
2009-01-01
ACTA METALLURGICA SINICA
Abstract:The research on scandium additions in aluminium alloys has gained some interests over the last decades,due to the precipitation of Al_3Sc phase particles,which have the beneficial effect on mechanical properties,weldability and corrosion resistance.But Sc is a very expensive strategic metal.Therefore,a breakthrough of the selection of RE is expected.However,only a limited number of possibilities exist in Al-based alloys for the formation of coherent strengthening particles that are thermodynamically stable and have the ordered,L1_2 structure.It involves the addition of some suitable alloying elements such as La,Ce,Y,Sc and especially to Sc,while the effects of other single elements are scarcely referred.Recent studies have considered Er as a promising alloying element in Al-alloy, and it has been shown that a small Er addition can improve the material properties in several Al-alloy systems.Most of the beneficial effects are attributed to the formation of the Al_3Er phase in these alloys. However,few research have been done on the effect of homogenizing treatment on the precipitation of Er modified 5083 alloy.Although the Al_3Sc and Al_3(Sc,Zr) particles are wildly studied,but few studies about coherency and coarsening behaviors of Al_3Er have been reported.The present investigation provides some information about orientation relationships of the precipitates with matrix and the coherency behavior of Al_3Er phase. Al_3Er phase precipitates during homogenizing of the Er modified 5083 alloy produced by direct chill casting were analyzed by transmission electron microscopy(TEM).The results show that many particles with different shapes and sizes precipitate during homogenizing.Spheric precipitates with the size between 10—50 nm is Al_3Er phase which arc good coherent/semi-coherent with matrix;the orientation relationships between matrix and the spheric precipitates are derived:[111]_m//[111]_(sp),(110)_m//(110)_(sp), (101)_m//(101)_(sp);[011]_m//[011]_s,(100)_m//(200)_(sp),where the indexs m and sp indicate matrix and spheric precipitate,respectivety. The radius for coherent/semi-conherent transition of Al_3Er particle is determinined as 12—20 nm by TEM analysis;The calculated value of critical transition radius(r_t=9.44 nm) of the Al_3Er precipitates is correspondent with the experiments.
What problem does this paper attempt to address?