Formation of ordered precipitates in Al-Sc-Er-(Si/Zr) alloy from first-principles study

Xiaomin Liu,Qian Wang,Chuan Zhao,Hongping Li,Mingliang Wang,Dong Chen,Haowei Wang
DOI: https://doi.org/10.1016/j.jre.2020.08.005
IF: 4.632
2021-05-01
Journal of Rare Earths
Abstract:Precipitate structure was Er-enriched core/Sc-enriched shell in Al-Sc-Er alloy.Precipitate stability order is independent on nucleation radius/atomic ratio/temperature.Core-shell structure precipitate showed better stability at particle radius ≥ 1 nm.Thermodynamic driving force for Si segregated in Al sublattice of Al<sub>3</sub>Er accelerated precipitation of (Al, Si)<sub>3</sub>Er.Thermodynamic driving force for Zr segregated in Al matrix accelerated precipitation of core-shell structure.The nucleation properties and stability of the ordered precipitates in Al-Sc-Er alloy were extensively studied by first-principles calculation. The calculated substitutional formation energy revealed that the dissolved Sc or Er in the Al matrix is very favorable to substitute the X sublattice site in L1<sub>2</sub>-Al<sub>3</sub>X (X = Sc/Er). The calculated solubility curve demonstrate the significant contribution of vibrational entropy to nucleation. The interface energies for Al/Al<sub>3</sub>Sc, Al/Al<sub>3</sub>Er and Al<sub>3</sub>Sc/Al<sub>3</sub>Er are calculated in the three directions of [100], [110] and [111], and find that the interface structure in (100) plane is the most desirable, and the interface energy of Al/Al<sub>3</sub>Er is the largest. Regardless of temperature and Sc/Er ratio, the L1<sub>2</sub>-Al<sub>3</sub>Sc<sub><em>x</em></sub>Er<sub>1-<em>x</em></sub> precipitation phase mainly formed as the core-shell structure with Al<sub>3</sub>Er as the core and Al<sub>3</sub>Sc as the shell due to lower nucleation energy. The core-shell structure behaved higher stability once the particle radius is greater than 1 nm. Furthermore, the thermodynamic driving force for the segregating of Si or Zr in Al-Sc-Er alloy should accelerate the precipitation kinetics, where Si partitions occurred preferentially to the Al<sub>3</sub>Er and Zr partitions preferentially to the Al matrix. Overall, these theoretical results can offer solid explanations to the available experimental results.The L1<sub>2</sub>-precipitation is predicted to exist in four candidate structures, including the isolated nucleation (L1<sub>2</sub>-Al<sub>3</sub>Sc and L1<sub>2</sub>-Al<sub>3</sub>Er), the homogeneous nucleation (L1<sub>2</sub>-Al<sub>3</sub>(Sc<sub><em>x</em></sub>Er<sub>1–<em>x</em></sub>)), the structures of Al<sub>3</sub>Sc-riched core and Al<sub>3</sub>Er-riched shell (core-shell Er(Sc)), and the structures of Al<sub>3</sub>Er-riched core and Al<sub>3</sub>Sc-riched shell (core-shell Sc(Er)). The order of nucleation stability is: core-shell Sc(Er) &gt; homogeneous Al<sub>3</sub>(Sc<sub><em>x</em></sub>Er<sub>1–<em>x</em></sub>) &gt; core-shell Er(Sc) &gt; isolated Al<sub>3</sub>Sc and Al<sub>3</sub>Er. The L1<sub>2</sub>-precipitation mainly formed as the core-shell structure with Al<sub>3</sub>Er as the core and Al<sub>3</sub>Sc as the shell due to lower nucleation energy. The core-shell structure behaves higher stability once the particle radius is greater than 1 nm.<span class="display"><span><ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1002072120303616-fx1_lrg.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download high-res image (252KB)</span></span></a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1002072120303616-fx1.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download full-size image</span></span></a></li></ol></span></span>
chemistry, applied
What problem does this paper attempt to address?