Formation and Relative Stabilities of Core-Shelled L12-Phase Nano-structures in Dilute Al–Sc–Er Alloys

Chaomin Zhang,Yong Jiang,Xiuhua Guo,Kexing Song
DOI: https://doi.org/10.1007/s40195-020-01096-y
2020-07-03
Acta Metallurgica Sinica (English Letters)
Abstract:<p class="a-plus-plus">First-principles thermodynamic calculations were carried out at the interface level for understanding the precipitation of coherent L1<sub class="a-plus-plus">2</sub>-phase nano-structures in dilute Al–Sc–Er alloys. All energetics, relevant to bulk substitution, interface formation, interfacial coherent strain and segregation, were calculated and used to evaluate the nucleation and relative stabilities of various possible L1<sub class="a-plus-plus">2</sub> nano-structures. Only matrix-dissolved solute Er (or Sc) can substitute Sc (or Er) in L1<sub class="a-plus-plus">2</sub>-Al<sub class="a-plus-plus">3</sub>Sc (or Al<sub class="a-plus-plus">3</sub>Er). The inter-substitution between L1<sub class="a-plus-plus">2</sub>-Al<sub class="a-plus-plus">3</sub>Sc and Al<sub class="a-plus-plus">3</sub>Er is not energy feasible. Ternary L1<sub class="a-plus-plus">2</sub>-Al<sub class="a-plus-plus">3</sub>(Er<sub class="a-plus-plus"><em class="a-plus-plus">x</em></sub>Sc<sub class="a-plus-plus">1−<em class="a-plus-plus">x</em></sub>) precipitates tend to form the Al<sub class="a-plus-plus">3</sub>Er-core and Al<sub class="a-plus-plus">3</sub>Sc-shell structure with a sharp core/shell interface. Three possible formation mechanisms were proposed and examined. The effects of Er/Sc ratio and aging temperature on the relative stabilities of L1<sub class="a-plus-plus">2</sub>-phase nano-structures in Al were also discussed.</p>
metallurgy & metallurgical engineering
What problem does this paper attempt to address?