Abstract:In this study, the effect of TiCN and WC-Co coatings on the tribological performance of spheroidal graphite cast iron materials was investigated by wear tests under dry and lubricated conditions. The mechanical and physical effects of the coating processes were analysed by microhardness measurements and visual methods (SEM, EDX, XRD). The tribological effect of WC-Co and TiCN coated specimens were investigated by ball-on-plate wear tests carried out under dry and boron oil emulsion (5% concentration) conditions at 50 N load and 60 rpm sliding speed parameters. The friction coefficient and wear volume results were obtained to investigate the effect of the coating process and boron oil emulsion on friction and wear behaviour. The wear mechanisms were determined with SEM images obtained from the worn surfaces and surfaces analysed elementally with EDX images. Additionally, surface morphology was examined with surface roughness measurements and 2D–3D topography images. According to the microhardness measurement results, it was observed that the spheroidal graphite cast iron with 290 HV hardness reached 1559 HV with TiCN coating and 1440 HV with WC-Co coating. According to the wear test results, it was determined that TiCN and WC-Co coatings decreased the friction coefficient by 32.51% and 12.80%, respectively. When the effect of boron oil usage compared to dry environmental conditions, it was concluded that the friction coefficient and wear volume decreased by a maximum of 54.80% and 53.70%, respectively. Additionally, the roughness values decreased in the experiments where the boron oil emulsion was used. However, although the TiCN coating improved the surface quality, the WC coating negatively affected the surface quality. Surface form images obtained with 2D and 3D topography also support the alteration in roughness values.

Wear Characteristics of Spheroidal Graphite Roll WC-8Co Coating Produced by Electro-Spark Deposition

Microstructure and properties of ESD coating on spheroidal graphite roll

Microstructure and properties of the YG8 ESD coating on a cast steel roll

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Preparation and tribological behaviours of graphite self-lubricating coating deposited on middle carbon steel by electrospark deposition

Microstructure and wear resistance of bimodal cemented carbide coating prepared by direct laser powder deposition

Nanostructured Ni–WC–Co composite coatings fabricated by electrophoretic deposition

Microstructure and Wear Behavior of Arc Sprayed Wc-Co/Fecrb and Wc-Ni/Fecrb Composite Coatings

Microstructure and Wear Performance of WC Reinforced Ni-based Composite Coating

Microstructure, Mechanical and Tribological Properties of WC-WCoB Coating

Microstructure and Tribological Property of Nanocrystalline Co–W Alloy Coating Produced by Dual-Pulse Electrodeposition

Microstructure and Properties of Coatings Deposited by Arc Spraying Cored Wires with Carbide Ceramic

Microstructure and Wear Performance of Arc Sprayed Fe-Feb-Wc Coatings

Accelerated Electrospark Deposition and the Wear Behavior of Coatings

Establishing Relationships Between Electrodeposition Techniques, Microstructure and Properties of Nanocrystalline Co–W Alloy Coatings

Investigation of wear behavior of carbide based coated rolling roll materials under dry and lubricated conditions

Preparation and Property Characterization of WS 2 Coatings Deposited on Micro-Nano Textured Surfaces of Cemented Carbide at Different WS 2 Target Currents

Characterization of Nano-Structured WC-Co Deposited by Cold Spraying

Microstructure and mechanical properties of CoCrFeMnNi/WC plasma deposited coating after the spark plasma sintering treatment

Comparative tribological study of air plasma sprayed WC–12%Co coating versus conventional hard chromium electrodeposit

Microstructure and wear properties of crystalline W alloy coatings prepared by electrodeposition