Effect of adding copper-plated graphite on the organization and wear reduction of copper-nickel alloy composite coatings
Shihong Ren,Xingchuan Xia,Kaihong Song,Jian Ding,Keping Geng,Guoxiong Song,Chenxu Huo,Yujie Wang,Weidan Liao,Nianxi Hua,Xueguang Chen
DOI: https://doi.org/10.1016/j.surfcoat.2024.131661
IF: 4.865
2024-12-12
Surface and Coatings Technology
Abstract:The aim is to improve the lubricating properties of surface of the joint hoop of the sucker rod In the oil industry. To achieve this, composite coatings of CuNi 25 alloy, incorporating varying amounts of copper-plated graphite, were applied to 40Cr steel substrates utilizing the laser cladding technique. The surface morphology, cross-sectional morphology, and composition of the coatings were examined to assess the impact of friction and wear performance on the copper-plated graphite-CuNi alloy self-lubricating coatings, as well as to elucidate the wear mechanisms involved. The resulting coatings exhibit a dense surface with uniform thickness, demonstrating excellent self-lubricating and wear-resistant properties during friction with counterpart components. As the proportion of copper-plated graphite rises, the quantity of graphite particles adhering to the surface of the coating also increases, thereby functioning as a solid lubricant. The mean microhardness of the coatings exhibited an increase from 245.2 HV 0.2 to 395.1 HV 0.2 , accompanied by an enhancement in the wear resistance of the coating surfaces. However, it was observed that as the friction frequency increased, the resistance to deformation diminished, the coefficient of friction decreased, and the self-lubricating properties were enhanced. It has been determined that the wear resistance and self-lubricating characteristics of copper-plated graphite‐copper‐nickel alloy self-lubricating coatings are influenced by the refinement of graphite particles and grains present on the surface of the coatings. The presence of graphite facilitates the refinement of grains within the coatings, thereby enhancing their hardness and wear-reducing capabilities. Furthermore, the predominant mode of wear observed in these coatings is identified as abrasive wear.
physics, applied,materials science, coatings & films