Abstract:After the converter steelmaking process, a considerable number of ferroalloys are needed to remove dissolved oxygen from the molten steel, but it also forms a lot of oxide inclusions that cannot be completely removed. At the same time, it increases the carbon emissions in the steel production process. After years of research, our team have developed a series of clean deoxidation technologies, including carbon deoxidation, hydrogen deoxidation, and waste plastic deoxidation of molten steel to address the aforementioned issues. In this study, thermodynamic calculations and laboratory experiments were employed to verify that carbon and hydrogen can reduce the total oxygen content in the molten steel melt to below 5 × 10 −6 and 10 × 10 −6 , respectively. An analysis of the deoxidation mechanisms and effects of polyethylene and polypropylene was also conducted. In addition, the applications of carbon deoxidation technology in different steels with the hot-state experiment and industrial production were discussed carefully. The carbon deoxidation experimental results of different steels were as follows: (1) the oxygen content of bearing steel was effectively controlled at 6.3 × 10 −6 and the inclusion number density was lowered by 74.73% compared to aluminum deoxidized bearing steel; (2) the oxygen content in gear steel was reduced to 7.7 × 10 −6 and a 54.49% reduction of inclusion number density was achieved with almost no inclusions larger than 5 μm from the average level of industry gear steels; (3) a total oxygen content of M2 high-speed steel was as low as 3.7 × 10 −6 . In industrial production practice, carbon deoxidation technique was applied in the final deoxidation stage for non-aluminum deoxidized bearing steel, and it yielded excellent results that the oxygen content was reduced to below 8 × 10 −6 and the oxide inclusions in the steel mainly consist of silicates, along with small amounts of spinel and calcium aluminate.

Control of Oxygen Content in 20CrMnTiH Gear Steel

Improvement of Key Production Processes of 20CrMnTi Gear Steel

Control of oxide inclusion for low carbon and low silicon steel

The Production Practice of Reducing the Oxygen Content in 42CrMo Steel

Development and prospects of molten steel deoxidation in steelmaking process

New steelmaking process based on clean deoxidation technology

Control of TiN precipitation behavior in titanium-containing micro-alloyed steel

Study on the technology of controlling nitrogen content in molten steel

Study of the relationship among total oxygen, inclusions and fatigue properties of gear steel

Research on TiN inclusion modification in 20CrMnTi gear steel by rare earth Ce during Si-Ca-Ba-Ce composite deoxidation

Continuous Cooling Phase Transformation Rule of 20crmnti Low-Carbon Alloy Steel

Control of Steel Composition and Evolution of Inclusions During Electroslag Remelting of NiCrMoV High‐Strength Steel

Study of an Economical and Effective Heat Treatment Method to Improve the Performance of Gear Steels

Control of Non-metallic Inclusion Plasticity and Steel Cleanliness for Ultrathin 18 Pct Cr-8 Pct Ni Stainless Steel Strip

Thermodynamics on compositional design of slag for the Ti content control in bearing steel

Effect of Carbon Content on Microstructure and Properties ofCr25 High-Chromium Cast Steel

Microstructure Characteristics and Wear Performance of a Carburizing Bainitic Ferrite + Martensite Si/Al-Rich Gear Steel

Effect of the Normalizing Temperature on the Size and Homogeneity of Austenite Grain in 20CrMnTi Carburized Gear Steel

Study on Internal Quality of Billets for 20crmntih Steel

Improvement of Mechanical Properties of 20CrMnTi Steel through Microstructure Modification

Influence of Controlling Rolling and Cooling on Oxide Scale of 65Mn Steel for Metallurgy Saw Blade