Refining Alnico 8 magnets with composition optimization of matrix phase, directional solidification and magnetic field annealing
Zhihao Liu,Deng Yongqiang,Sajjad Ur Rehman,Liu Haihua,Abdul Jabbar Khan,Zhong Shuwei,Xiaoqiang Yu,Yang Munan
DOI: https://doi.org/10.1016/j.jallcom.2024.176329
IF: 6.2
2024-09-08
Journal of Alloys and Compounds
Abstract:Optimized shape anisotropy of the Fe-Co rich ferromagnetic (α 1 ) phase and the effective separation of the α 1 and α 2 phases with maximum magnetization difference—where α 2 represents a paramagnetic magnetic phase—are the key parameters for maximizing the magnetic properties of Alnico magnets. In this manuscript, efforts have been undertaken to optimize the shape anisotropy of the α 1 phase and increase the difference in magnetization and separation between α 1 and α 2 phases by fine tuning Al and Ni contents, directional solidification and magnetic field annealing methods. At first, Alnico magnets were fabricated by adjusting the content of α 2 phase followed by homogenization, magnetic field annealing at high temperature, and low-temperature tempering. Intrinsic coercivity ( H cj ) of ⁓146.0 kA/m, remanence ( B r ) of ⁓0.90 T and maximum energy density ( (BH) max ) of 46.02 kJ/m 3 are achieved in the magnet with 8.2 wt% Al and 12.8 wt% Ni treated in field of 1.5 T for 10 minutes. At the second stage, the magnet with optimal magnetic properties is directionally solidified to develop columnar grains, and then the α 1 phase is grown in the direction of the columnar grains by magnetic field annealing to enhance the (BH) max to 79.8 kJ/m 3 . The axial ratio of the α 1 phase increased significantly with the increase of the grain size, particularly in the directionally solidified magnets. The Curie temperature of the α 1 phase is noted near 1150 K, while the Curie temperature of the α 2 phase is below 400 K. The magnets demonstrated excellent temperature stability, with magnetic properties decreasing by only 10–12 % at 800 K. These results may pave the way for further development of Alnico magnets specifically for high temperature applications.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering