Abstract:Mesoporous carbon materials with ultra-thin carbon pore walls and highly dispersed Ni nanoparticles have been successfully prepared by using two different SBA-15 silicas as hard templates and 2,3-dihydroxynaphthalene (DHN) as a carbon precursor. The nickel precursor was a concentrated nickel nitrate hexahydrate [Ni(NO3)(2)center dot 6H(2)O] solution in 2-propanol, which was added to the carbon-silica nanocomposite prior to thermal treatment. The samples studied were analyzed by thermogravimetry (TG), nitrogen adsorption at -196 degrees C, powder X-ray diffraction (XRD), Raman spectroscopy, scanning and transmission electron microscopy (STEM), and in situ electron diffraction X-ray spectroscopy (EDX). While TG analysis revealed carbon contents lower than 30 wt.-%, nitrogen adsorption provided information about the homogeneity of the carbon thin film deposited onto the mesopore walls of the ordered silica templates SBA-15. The templates, carbon-silica nanocomposites, and carbon inverse replicas with nickel nanoparticles exhibit uniform pores, high surface areas, and large pore volumes. Partially graphitic carbon was identified by the presence of a characteristic G band in the Raman spectra, whereas the diffraction peak attributed to the stacking of graphene planes was not observed by powder XRD. The presence of ordered domains in the carbon materials studied was confirmed by small angle XRD and STEM imaging. In addition, the STEM images revealed that the nickel nanoparticles are uniform in size, ca. 3 nm, and are homogeneously dispersed on the tubular carbon walls. A few larger clusters of nickel, ca. 60 nm, present on the external surface, were identified by powder XRD as metallic Ni. The in situ EDX revealed that the small nanoparticles are largely composed of Ni with traces of NiO. Similar nanoparticle dispersions have been reported only for Ni-containing multiwalled carbon nanotubes (CNTs), whereas previously reported ordered mesoporous carbon materials, CMK-3, possess larger Ni/NiO nanoparticles. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2009)

Synthesis and Characterization of Graphite Nanofibers Deposited on Nickel Foams

SYNTHESIS AND HYDROGEN ADSORPTION OF FISH-BONE GRAPHITE NANOFIBERS

Nickel Nanoparticles Embedded in Porous Carbon-Coated Honeycomb Ceramics: A Potential Monolithic Catalyst for Continuous Hydrogenation Reaction

Methane Catalytic Cracking to Make Hydrogen and Graphitic Nano Carbons (nanotubes, Microfibers, Microballs, Onions) with Zero Emission

Large-Scale Synthesis of Herringbone Carbon Nanofibers on Nonsupported Nickel Catalyst

Preparation and Characterization of a Graphite Electrode Containing Carbon Nanotubes Grown in Situ by Flame Synthesis

Growth of well-crystallized segmented graphite nanofibers by catalytic chemical vapor deposition

Preparation of Carbon Nanofibers over Carbon Nanotube-Nickel Catalyst in Propylene Decomposition

Conformation and Microstructure of Carbon Nanofibers Deposited on Foam Ni

Synthesis Of Nickel Nanoparticles And Carbon Encapsulated Nickel Nanoparticles Supported On Carbon Nanotubes

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

Synthesis of Ni3S2 nanotube arrays on nickel foam by catalysis of thermal reduced graphene for hydrogen evolution reaction

Mesoporous Carbon Materials with Ultra‐Thin Pore Walls and Highly Dispersed Nickel Nanoparticles

Preparation and Performance of the Lipid Hydrodeoxygenation of a Nickel-Induced Graphene/HZSM-5 Catalyst

A Catalytic Etching-Wetting-Dewetting Mechanism in the Formation of Hollow Graphitic Carbon Fiber

Synthesis of carbon nanofibers by CVD as a catalyst support material using atomically ordered Ni3C nanoparticles

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Preparation of Ni–Cu Catalyst for Carbon Nanofiber Production by the Mechanochemical Route

Pyrolytic Synthesis of Carbon Nanotubes on Ni, Co/MCM-41 Catalysts

Study on Carbon Nanotubes of Pyrolysis Carbons P for In Situ Catalytic Formation on Expanded Graphite Surface