Abstract:Carbon nanofibers (CNFs) were synthesized by CO disproportionation on iron catalyst at CO concentration between 58.3% and 75.0%, H2 concentration between 8.3% and 25.0% and reaction temperature between 833 and 913K. The time-depending rate of CNFs growth as a function of time was determined by an on-line mass spectrometer and the morphologies of all CNFs products were observed by electronic microscopy. Not only the CNFs growth rate but also the morphology of the grown CNFs were shown to vary with the three operating variables. SEM and TEM images showed that the three-dimensional morphologies of the CNFs were twist, helical or straight and an interesting relationship between the maximal growth rate and the morphology was observed. When the growth rate was between 0.8 and 0.9mmol/(sgcat), the CNFs were twist. As the growth rate increased to 1.0mmol/(sgcat), more helical nanofibers appeared. Straight nanofibers were produced when the growth rate reached the level of 1.2mmol/(sgcat). Finally when the rate of CNFs growth was high at 1.8mmol/(sgcat), the absolute majority of the solid products was amorphous carbon coexisting with some short and thick nanofibers. Under different operating conditions, the crystal faces of the catalysts had different anisotropy properties for carbon deposition, thus producing CNFs with different morphologies.

Large-Scale Synthesis of Herringbone Carbon Nanofibers on Nonsupported Nickel Catalyst

Synthesis and Characterization of Graphite Nanofibers Deposited on Nickel Foams

Synthesis of carbon nanofibers by CVD as a catalyst support material using atomically ordered Ni3C nanoparticles

Synthesis of Carbon Nanostructures with Different Morphologies by Cvd of Methane

Temperature-Dependent Chemical State of the Nickel Catalyst for the Growth of Carbon Nanofibers

Controllable preparation of Ni nanoparticles for catalysis of coiled carbon fibers growth.

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

The Efficient Synthesis of Carbon Nano-Onions Using Chemical Vapor Deposition on an Unsupported Ni–Fe Alloy Catalyst

Unconventional Ni–P Alloy-Catalyzed CVD of Carbon Coil-Like Micro- and Nano-Structures

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

Robust Growth of Herringbone Carbon Nanofibers on Layered Double Hydroxide Derived Catalysts and Their Applications As Anodes for Li-Ion Batteries

Controllable synthesis of carbon coils and growth mechanism for twinning double-helix catalyzed by Ni nanoparticle

Fabrication and Growth Mechanism of Carbon Nanotubes by Chemical Vapor Deposition

Selective Synthesis of Carbon Nanofibers with Various Structures Through the Catalytic Pyrolysis of Ethylene

Synthesis of Carbon Nanofiber Monoliths by Chemical Vapor Deposition

Large‐scale Synthesis of Hafnium Carbide Nanowires Via a Ni‐assisted Polymer Infiltration and Pyrolysis

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

Highly Efficient Synthesis of Carbon Nanocoils by Catalyst Particles Prepared by a Sol–gel Method

Kinetically Controlled Synthesis of Carbon Nanofibers with Different Morphologies by Catalytic CO Disproportionation over Iron Catalyst

Recent Advances in Synthesis of Reshaped Fe and Ni Particles at the Tips of Carbon Nanofibers and Their Catalytic Applications