Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Synthesis of Helical Carbon Nanotubes, Worm-Like Carbon Nanotubes and Nanocoils at 450 °C and Their Magnetic Properties

Large‐Scale Synthesis, Annealing, Purification, and Magnetic Properties of Crystalline Helical Carbon Nanotubes with Symmetrical Structures

Characterization and Magnetic Properties of Helical Carbon Nanotubes and Carbon Nanobelts Synthesized in Acetylene Decomposition over Fe−Cu Nanoparticles at 450 °C

High Magnetization Helical Carbon Nanofibers Produced by Nanoparticle Catalysis

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

Helical Carbon Nanotubes: Catalytic Particle Size-Dependent Growth and Magnetic Properties

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Large-scale Synthesis, Characterization and Microwave Absorption Properties of Carbon Nanotubes of Different Helicities

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Large-Scale Synthesis and Magnetic Property of Carbon Nanotubes

Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes

Synthesis of Plait-Like Carbon Nanocoils in Ultrahigh Yield, and Their Microwave Absorption Properties

A New Method to Fabricate Large Amount of Single-Walled Carbon Nanotubes

Controllable Synthesis, Characterization, and Magnetic Properties of Magnetic Nanoparticles Encapsulated in Carbon Nanocages and Carbon Nanotubes

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

Functionalization of carbon nanotubes with magnetic nanoparticles: general nonaqueous synthesis and magnetic properties.

Magnetic Properties and Large-Scale Synthesis of Novel Carbon Nanocomposites Via Benzene Decomposition over Ni Nanoparticles

Large-Scale Synthesis of Herringbone Carbon Nanofibers on Nonsupported Nickel Catalyst

Synthesis and Properties of Magnetic Composites of Carbon Nanotubes/Fe Nanoparticle

Controllable and Large-Scale Synthesis of Carbon Nanofibers, Bamboo-Like Nanotubes, and Chains of Nanospheres over Fe/Sno2 and Their Microwave-Absorption Properties

Synthesis, Photoluminescence, and Magnetic Properties of Nitrogen-Doping Helical Carbon Nanotubes