Abstract:The possibility of preparing straight multi-walled carbon nanotubes (MWCNTs) on a large scale is demonstrated using direct current arc discharge with a rotating graphite anode in low pressure air. The process is time-saving, economical, and non-hazardous. It is found that the optimum air pressure for the highest yield of MWCNTs is about 60 Torr. Investigation of the internal organization of the cathode deposit reveals that many columns about 40 μm in diameter are closely packed and mechanically stable. The highest content of MWCNTs is found in the intercolumnar spaces between columns. Emitters made of the cathode deposits that contain a large number of straight nanotubes exhibit outstanding field emission properties. The turn-on electric field decreases from 1.44 to 0.93 V/μm and the field enhancement factor β increases from about 3,190 to 7,830 only after simple burning at 750 °C for 30 min in air. The results indicate that MWCNTs prepared by arc discharge in air are promising for field emission application.

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

A Novel Method to Produce Large Amount Single-Walled Carbon Nanotubes by Arc Discharging

Large Scale Synthesis of Single-Wall Carbon Nanotubes by Arc-Discharge Method

An Efficient Method to Produce Single-Walled Carbon Nanotubes by Round-Trip Arc Discharge

A New Method to Fabricate Large Amount of Single-Walled Carbon Nanotubes

Preparation of Large Amounts of Carbon Nanotubes in Hydrogen Atmosphere by Arc-Discharge

Synthesis of Single-Walled Carbon Nanotube Films with Large Area and High Purity by Arc-Discharge

Direct Synthesis of High Purity Single-Walled Carbon Nanotube Fibers by Arc Discharge

Mass-production of single-wall carbon nanotubes by arc discharge method

Large Scale and High Purity Synthesis of Single-Walled Carbon Nanotubes by Arc Discharge at Controlled Temperatures

Synthesis of high quality single-walled carbon nanotubes by arc discharge method in large scale

Mass-production of Single-Wall Carbon Nanotubes by Arc Discharge Method11this Work Was Supported by the National Natural Science Foundation of China, No. 29671030.

Synthesis of High Quality Single-Walled Carbon Nanotube Silks by the Arc Discharge Technique

Carbon Nanotubes Grown on the Surface of Cathode Deposit by Arc Discharge

Low-cost Synthesis of Single-Walled Carbon Nanotubes by Low-Pressure Air Arc Discharge

Purification and characterization of single-walled carbon nanotubes produced by arc-discharge

Large-scale Synthesis of Single-Walled Carbon Nanohorns by Submerged Arc

Synthesis of Straight Multi-Walled Carbon Nanotubes by Arc Discharge in Air and Their Field Emission Properties

Length-controlled synthesis of single-walled carbon nanotubes by arc discharge with variable cathode diameters

Synthesis of single -walled carbon nanotubes in reduced air atmosphere by DC arc discharge

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation