In Situ Synthesis of Super-Long Cu Nanowires Inside Carbon Nanotubes with Coal As Carbon Source
Zhiyu Wang,Zongbin Zhao,Jieshan Qiu
DOI: https://doi.org/10.1016/j.carbon.2006.04.001
IF: 10.9
2006-01-01
Carbon
Abstract:Nano-sized copper wires have received considerable attention because of their potential applications in next generation electronic nanodevices in future [1,2]. Up to now, a number of approaches including vapor depositions [1], template synthesis [2,3], solution-phase reactions [4,5] and vapor–solid reaction growth (VSRG) [6] have been developed for making copper nanowires. Despite of the great progresses, some tough problems related to the quality of copper nanowires such as poor oxidation resistance and crystallinity, short length, and nonlinear morphology still need to be addressed [1–7]. Carbon nanotubes (CNTs) are believed to be a good template for making Cu nanowires with perfect 1D morphology and good stability, and this idea has been tested by arc discharge in hydrogen [8] or microwave plasma-assisted CVD [9]. Here, we report a simple arc-discharge method for in situ synthesis of Cu-filled CNTs with coal as carbon precursor. It has been found that super-long crystalline Cu nanowires, of which the average length is over several tens of micrometers and the aspect ratio is ca. 200–360, can be directly fabricated inside the CNTs in large quantity. The preparation experiments were conducted in a traditional DC arc-discharge reactor in argon atmosphere. A high purity graphite tube (10 mm OD, 6 mm ID) filled with a mixture of anthracite coal (from Yunnan Province, China) and CuO powders (6150 lm in size) was used as consuming anode while the cathode was a high purity graphite rod (15 mm OD). The weight ratio of CuO to coal powder in the mixture was 1:9. For each run that normally lasted about 15 min, the arc discharge was conducted with DC current of 70 A and voltage of 20 V in argon at 0.08– 0.09 MPa. After the arc discharge was over, the deposits on the cathode were collected and examined using transmission electron microscopy (TEM, JEM-2000EX; HRTEM, Philips Tecnai G 20). Fig. 1a shows a typical low magnification TEM image of the as-prepared sample, revealing the successful synthesis of CNT-encapsulated nanowires with a length of over several tens of micrometers. It has been found that in some nanowires there are several distorted defects such as kinks and curls, between which the distance varies in a range from hundreds of nanometers to several micrometers. Further high magnification TEM examination (see Fig. 1b) shows that the CNTs are completely filled with continuous nanowires with a diameter ca. 30–80 nm. The aspect ratio of these carbon coated nanowires is 200–360, which is much higher than those reported previously in the literature [8,9]. The repeated experiments indicate that on average, more than 40–50% of the as-prepared CNTs are filled with nanowires, as can be seen in Fig. 2. The selected area electron diffraction (SAED) patterns taken from the nanowires between the distorted section are shown in insets of Figs. 2b and d, showing the diffraction as regular arrays of sharp spots together with the short arc due to the