Abstract:To in situ grow carbon nanotubes (CNTs) on the surface of carbon fibre fabric (CFF) with suitable diameter and uniform distribution, controllable catalyst deposition is the key process. A controllable and non-destructive pre-treatment, that is, electrochemical oxidation pre-treatment, was explored to facilitate uniform `seeding` nano-sized catalyst particles on the surface of CFF without causing damage to carbon fibres. Main factors, such as voltage, concentration of electrolyte, electrolytic time, catalyst type and concentration of the catalyst precursor, were investigated. X-ray photoelectron spectroscopy tests indicated that voltage, concentration of electrolyte and duration of electrochemical treatment determined the distribution density of catalyst nanoparticles by controlling the concentration of the functional groups, while the diameter of catalyst particles was decided by the concentration of Fe(NO3)3 and CO(NH2)2. Besides, the diameter of catalyst particles could be modulated by adding Al(NO3)3 in the solution of the catalyst precursor. At the same time, to avoid cementite produced during the calcination and reduction process, the temperature should be controlled below 773 K. Scanning electron microscopy observations indicated that well-dispersed in situ grown CNTs could be obtained after CFF had been chemical oxidised at the voltage of 10 V for 10 s with 0.02 M NH4HCO3 as electrolyte and followed by catalyst deposition.

Preparation and Characterization of a Graphite Electrode Containing Carbon Nanotubes Grown in Situ by Flame Synthesis

In Situ Fabrication and Graphitization of Amorphous Carbon Nanowires and Their Electrical Properties

Preparation and Characterization of the Carbon Nano Tubes Supporting Oxygen Electrode Material for PEMFC

Confined Growth of Carbon Nanotubes in Nanocutting Channel on Highly Oriented Pyrolytic Graphite

Preparation, Structure and Electrochemical Hydrogenation of Carbon Nanotubes Supported Platinum Catalysts

Mechanism of carbon nanotube growth in expanded graphite via catalytic pyrolysis reaction using carbores P as a carbon source

Carbon Nanotubes Grown on the Surface of Cathode Deposit by Arc Discharge

Electrochemical co-deposition of carbon nanotube/Ni composite layer

Growth of well-crystallized segmented graphite nanofibers by catalytic chemical vapor deposition

The Role of the Catalytic Particle in the Growth of Carbon Nanotubes by Plasma Enhanced Chemical Vapor Deposition

Catalyst-Free in Situ Carbon Nanotube Growth in Confined Space Via High Temperature Gradient

One-step preparation of a N-CNTs@Ni foam electrode material with the co-production of H2 by catalytic reforming of N-containing compound of biomass tar

Synthesis and Characterization of Graphite Nanofibers Deposited on Nickel Foams

Non-destructive and controllable catalyst deposition of in situ growing carbon nanotubes onto the carbon fibre fabric

EXPERIMENTAL RESEARCH ON SYNTHESIS OF CARBON NANOTUBES

Application of NiO deposited by atomic layer deposition for carbon nanotubes catalytic growth

In situ growth of CNTs on carbon fiber by chemical vapor deposition

Field emission and thermo-electrochemical cell performances of various types of carbon nanotubes

In situ growth of N-doped carbon nanotubes from the products of graphitic carbon nitride etching by nickel nanoparticles

Multistage carbon nanotubes grown on foamed nickel with organic solutions as multifunctional high performance electrodes

Synthesis,Characterization and Performance of Helical Carbon Nanotubes