Abstract:Carbon nanofibers (CNFs) are prepared from electrospun polyacrylonitrile (PAN) because of their high carbon content. Heat treatment (oxidative stabilization and carbonization) is necessary to convert PAN nanofibers into CNFs. The fixation of fibrous structure of polymer precursor during heat treatment is always considered as a problem. The aim of this work is to study the effects of two different stabilization temperatures and fixation on CNFs prepared from electrospun PAN nanofibers. In this study, we use two different stabilization temperatures (275 and 300 °C) to investigate the effect of temperature on the oxidation, cyclization, crosslinking, aromatization, and dehydrogenation processes that occur during the stabilization heat treatment. Further, we study the effect of electrospun sheet fixation during heat treatment on the fibrous structure of electrospun fibers and methods to prevent shrinkage and folding of the electrospun sheet. Fourier transform infrared spectroscopy revealed the effectiveness of stabilization at 300 °C when transforming PAN elctrospun nanofibers to CNFs. Raman spectroscopy showed that carbonization at 800 °C after stabilization at 300 °C lowers the R-value (ID/IG ratio) comparing with that stabilized at 275 °C which indicates increasing the amount of structurally ordered graphite crystallites relative to the disordered structure. Scanning electron microscopy (SEM) revealed that fixation process maintained a uniform fibrous structure for the stabilized sheets without shrinkage, whereas carbonization at 800 °C without fixation resulted in deformed and folded carbonized PAN with loss in the fibrous structure.

Conformation and Microstructure of Carbon Nanofibers Deposited on Foam Ni

Enhanced Interfacial Properties of High-Modulus Carbon Fiber Composites Via Molecular Assembly on Fiber Surface

Carbon-nanotube-templated Carbon Nanofibers with Improved Mechanical Performance

Synthesis and Characterization of Graphite Nanofibers Deposited on Nickel Foams

Growth of well-crystallized segmented graphite nanofibers by catalytic chemical vapor deposition

Preparation of Carbon Nanofibers over Carbon Nanotube-Nickel Catalyst in Propylene Decomposition

Understanding Macroscopic Assemblies of Carbon Nanostructures with Microstructural Complexity

Nano-octopus: a new form of branching carbon nanofiber

Rapid and Scalable Synthesis of Novel Carboxylated Aramid Nanofibers for Simultaneously Improving the Strength and Toughness of Carbon Fiber/epoxy Laminates

Long Bundles of Aligned Carbon Nanofibers Obtained by Vertical Floating Catalyst Method

Influence of Carbon Nanotube Coatings on Carbon Fiber by Ultrasonically Assisted Electrophoretic Deposition on Its Composite Interfacial Property.

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Nanoporous Structured Submicrometer Carbon Fibers Prepared Via Solution Electrospinning of Polymer Blends.

Dependence of Carbon Fiber Morphology with Deposition Conditions

Hexagonal Crystalline Nanofillers Reinforced Composite Carbon Nanofibers with Optimized Crystal Structure and Improved Mechanical Properties

Investigation of Microstructures of Znco2o4 on Bare Ni Foam and Ni Foam Coated with Graphene and Their Supercapacitors Performance

Diamond-Like Carbon Nanofoam from Low-Temperature Hydrothermal Carbonization of a Sucrose/Naphthalene Precursor Solution

Synthesis,Characterization and Performance of Helical Carbon Nanotubes

Properties of Carbon Nanofibers Prepared from Polyacrylonitrile/Poly(methyl Methacrylate) Blend

Fractal carbon nanotube fibers with mesoporous crystalline structure

The effect of using two stabilization temperatures and fixation process on preparation of carbon nanofibers