Abstract:Hypothesis: Zirconia microparticles produced by sol-gel synthesis have great potential for photonic applications. To this end, identifying synthetic methods that yield reproducible control over size uniformity is important. Phase transformations during thermal cycling can disintegrate the particles. Therefore, understanding the parameters driving these transformations is essential for enabling high-temperature applications. Particle morphology is expected to influence particle processability and stability. Yttria-doping should improve the thermal stability of the particles, as it does in bulk zirconia. Experiments: Zirconia and YSZ particles were synthesized by improved sol-gel approaches using fatty acid stabilizers. The particles were heated to 1500 °C, and structural and morphological changes were monitored by SEM, ex situ XRD and high-energy in situ XRD. Findings: Zirconia particles (0.4-4.3 μm in diameter, 5-10% standard deviation) synthesized according to the modified sol-gel approaches yielded significantly improved monodispersities. As-synthesized amorphous particles transformed to the tetragonal phase at ∼450 °C with a volume decrease of up to ∼75% and then to monoclinic after heating from ∼650 to 850 °C. Submicron particles disintegrated at ∼850 °C and microparticles at ∼1200 °C due to grain growth. In situ XRD revealed that the transition from the amorphous to tetragonal phase was accompanied by relief in microstrain and the transition from tetragonal to monoclinic was correlated with the tetragonal grain size. Early crystallization and smaller initial grain sizes, which depend on the precursors used for particle synthesis, coincided with higher stability. Yttria-doping reduced grain growth, stabilized the tetragonal phase, and significantly improved the thermal stability of the particles.

Synthesis and Characteristic of Hierarchically Porous Zirconium Oxide Doped with Yttrium

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Synthesis, Characterization and Crystal Structure Analysis of an Open-Framework Zirconium Phosphate

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Optimization of the structure and morphology of monoclinic phase nanoscale zirconium dioxide

Synthesis and Characterization of Yttria-Doped Mesoporous Zirconia

Hierarchically porous zirconium dioxide dual-templated by acacia mangium tannin extract and an amphiphilic triblock copolymer

Preparation and Characterization of Three-Dimensionally Ordered Macroporous Yttria-Stabilized Zirconia by Aqueous Organic Gel Route

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

A Novel Way to Fabricate Highly Porous Fibrous YSZ Ceramics with Improved Thermal and Mechanical Properties

Fabrication and Properties of Porous Yttria-Stabilized Zirconia Ceramics

A Composite Surfactant Route for the Synthesis of Thermally Stable and Hierarchically Porous Zirconia with a Nanocrystallized Framework.

Preparation and Characterization of Hierarchically Porous Monolithic TiO2

Structure and thermal stability of mesostructured zirconium oxophosphates

Ultrafine-grained High-Entropy Zirconates with Superior Mechanical and Thermal Properties

Fabrication and properties of a stable and porous YSZ/nano-HA structure by binder jetting processes

Mesoporous Yttria-Zirconia Solid Solution with Improved Textural Properties Prepared Via Lauric Acid-Assisted Synthesis

Preparation of Porous Spodumene/zircon Composite Ceramics and Its Thermal and Mechanical Properties

Effect of Doping Location Induced Anisotropy on Thermophysical Properties of Dilute Fe2O3‐Y2O3‐ZrO2 Solid Solutions

Synthesis and thermal stability of zirconia and yttria-stabilized zirconia microspheres

Preparation and stereolithography 3D printing of ultralight and ultrastrong ZrOC porous ceramics