Abstract:The single-crystalline LiMn2O4 nanorods were successfully synthesized by a simple, low-cost and eco-friendly approach in which the γ-MnOOH nanorods were prepared through a facile hydrothermal process, in which KMnO4 was reduced by anhydrous alcohol (CH3CH2OH) without adding any template reagent or additional surfactant. The crystal structures and morphologies of synthesized materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), respectively. The results showed that the γ-MnOOH nanorods had high crystallinity and well-shaped morphology with an average diameter of 200nm and an average length of 12μm. For the resulting LiMn2O4 nanorods, the electrochemical properties were investigated by galvanostatic charge-discharge test, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). For the optimal LiMn2O4 nanorods, the initial discharge capacity was 123.5mAhg−1 and remained 110.2mAhg−1 after 100 cycles at 1.0C in the voltage range of 3.20∼4.35V. Moreover, the optimal LiMn2O4 nanorods can present superior rate performance, especially the capacity recovery performance as the charge-discharge rate restores to 0.1C from 5.0C. Such excellent electrochemical performance could make them to be the promising cathode material for high performance lithium-ion batteries.

Synthesis and Electrochemical Properties of Single-Crystalline Liv3o8 Nanorods As Cathode Materials for Rechargeable Lithium Batteries

Synthesis and Electrochemical Properties of Single-Crystalline Liv3o8 Nanobelts for Rechargeable Lithium Batteries

Synthesis and Electrochemical Performance of Rod-Like Liv3o8 Cathode Materials for Rechargeable Lithium Batteries

Facile synthesis of NaV6O15 nanorods and its electrochemical behavior as cathode material in rechargeable lithium batteries

Electrochemical behavior and structural stability of LiV3O8 microrods as cathode for lithium-ion batteries

Graphene-nanosheet-wrapped LiV3O8 Nanocomposites As High Performance Cathode Materials for Rechargeable Lithium-Ion Batteries

In Situ Synthesis of Liv3o8 Nanorods on Graphene As High Rate-Performance Cathode Materials for Rechargeable Lithium Batteries

Mesoporous Single-Crystalline V2o5 Nanorods Assembled into Hollow Microspheres As Cathode Materials for High-Rate and Long-Life Lithium-Ion Batteries

High Capacity and Enhanced Structural Reversibility of Β-Lixv2o5 Nanorods As the Lithium Battery Cathode

LiMn2O4 Nanorods As a Super-Fast Cathode Material for Aqueous Rechargeable Lithium Batteries

A Simple, Low-Cost and Eco-Friendly Approach to Synthesize Single-Crystalline Limn2o4 Nanorods with High Electrochemical Performance for Lithium-Ion Batteries

Electrochemical Behavior of Alpha-Moo3 Nanorods As Cathode Materials for Rechargeable Lithium Batteries.

Hydrothermal synthesis and rate capacity studies of Li3V2(PO4)3 nanorods as cathode material for lithium-ion batteries

In situ soft-chemistry synthesis of beta-Na0.33V2O5 nanorods as high-performance cathode for lithium-ion batteries

An amorphous wrapped nanorod LiV3O8 electrode with enhanced performance for lithium ion batteries

Revealing mechanism responsible for structural reversibility of single-crystal VO2 nanorods upon lithiation/delithiation

Superior Stability and Dynamic Performance of Single Crystal LiNi1/3Co1/3Mn1/3O2 Nanorods from Β-Mno2 Template for Lithium-Ion Batteries

Single-Crystal H2v3o8 Nanowires: A Competitive Anode with Large Capacity for Aqueous Lithium-Ion Batteries

Electrochemical Characteristics of Lithium Vanadate, Li3VO4 As a New Sort of Anode Material for Li-ion Batteries

Synthesis and Electrochemical Properties of Nav3o8 Nanoflakes As High-Performance Cathode for Li-Ion Battery

A Large Capacity of LiV3O8 Cathode Material for Rechargeable Lithium-Based Batteries