Abstract:Li3V2(PO4)3 cathodes for Li-ion batteries (LIBs) were synthesized using a hydrothermal method with the subsequent annealing in an argon atmosphere to achieve optimal properties. The X-ray diffraction analysis confirmed the material's single-phase nature, while the scanning electron microscopy revealed a granular structure, indicating a uniform particle size distribution, beneficial for electrochemical performance. Magnetometry and electron spin resonance studies were conducted to investigate the magnetic properties, confirming the presence of the relatively low concentration and highly uniform distribution of tetravalent vanadium ions (V4+), which indicated low lithium deficiency values in the original structure and a high degree of magnetic homogeneity in the sample, an essential factor for consistent electrochemical behavior. For this pure phase Li3V2(PO4)3 sample, devoid of any impurities such as carbon or salts, extensive electrochemical property testing was performed. These tests resulted in the experimental discovery of a remarkably high lithium diffusion coefficient D = 1.07 × 10−10 cm2/s, indicating excellent ionic conductivity, and demonstrated impressive stability of the material with sustained performance over 1000 charge–discharge cycles. Additionally, relithiated Li3V2(PO4)3 (after multiple electrochemical cycling) samples were investigated using scanning electron microscopy, magnetometry and electron spin resonance methods to determine the extent of degradation. The combination of high lithium diffusion coefficients, a low degradation rate and remarkable cycling stability positions this Li3V2(PO4)3 material as a promising candidate for advanced energy storage applications.

A Large Capacity of LiV3O8 Cathode Material for Rechargeable Lithium-Based Batteries

Synthesis and Electrochemical Performance of Rod-Like Liv3o8 Cathode Materials for Rechargeable Lithium Batteries

Non-destructive Chemical Prelithiation of VO2(B) Anodes Constructing a Multifunctional Interphase Layer for Advanced Li-Ion Batteries

Synthesis and Electrochemical Properties of Single-Crystalline Liv3o8 Nanorods As Cathode Materials for Rechargeable Lithium Batteries

Synthesis and Electrochemical Properties of Single-Crystalline Liv3o8 Nanobelts for Rechargeable Lithium Batteries

Enhanced electrochemical properties of Al2O3-coated LiV3O8 cathode materials for high-power lithium-ion batteries

Electrochemical performance of the carbon coated Li3V2(PO4)3 cathode material synthesized by a sol–gel method

Preparation and Characterization of Spherical Li3v2 (po4)(3)/c Cathode Material for Lithium-Ion Batteries

Polyacrylamide-assisted freeze drying synthesis of hierarchical plate-arrayed LiV3O8 for high-rate lithium-ion batteries

An elaborate insight of lithiation behavior of V2O5 anode

Synthesis and Electrochemical Performance of Li1+xV3O8 As Cathode Material for Lithium Secondary Batteries

MgV3O8 Anode Exhibiting Enhanced Rate Capability and Stability for Lithium Storage Applications

Synthesis Method, High Lithium Diffusion Coefficient and Magnetic Inhomogeneity

Facile synthesis of LiVO3 and its electrochemical behavior in rechargeable lithium batteries

High Capacity and Excellent Cyclability of Vanadium (IV) Oxide in Lithium Battery Applications

Revealing the Role of NH4VO3 Treatment in Ni-rich Cathode Materials with Improved Electrochemical Performance for Rechargeable Lithium-Ion Batteries

Preparation and electrochemical properties of spherical Li1+xV3O8

A Li3V2(PO4)3/C Thin Film with High Rate Capability As a Cathode Material for Lithium-Ion Batteries

Porous Monodisperse V2O5 Microspheres As Cathode Materials for Lithium-Ion Batteries

ChemInform Abstract: Freeze‐Drying Synthesis of Li3V2(PO4)3/C Cathode Material for Lithium‐Ion Batteries.

Synthesis and electrochemical performance of Li 1.131Mn 0.504Ni 0.243Co 0.122O 2 cathode materials for lithium ion batteries via freeze drying