Abstract:The Zr0.84Y0.16O1.92 (YSZ)–La0.8Sr0.2Cr0.5Fe0.5O3−δ (LSCrF) composite membrane was prepared using the phase inversion tape casting method. Two slurries, one composed of YSZ and LSCrF powder, and the other composed also graphite, were used for preparation of the membrane. They were co-tape cast onto a Mylar sheet, and then immersed in a water bath for solidification into a green tape through phase inversion mechanism. After sintering at 1450°C in the air, the green tape was converted into a ceramic membrane. The sintered membrane possessed an asymmetric structure: a dense layer of thickness ~30μm and a finger-like porous support of thickness ~1mm. The membrane was further modified by applying a porous YSZ–LSCrF layer on its surfaces at the dense layer side and depositing Sm0.2Ce0.8O2 nano-particles on the inner surfaces of the support. The oxygen permeability of the as-prepared membrane was measured by exposing its dense layer side to air and the support side to CO at elevated temperatures. The membrane exhibited desired oxygen permeability under the given measurement conditions. An oxygen permeation flux as large as 2.4ml·cm−2·min−1 (STP) was observed at 900°C, which is comparable to the hollow fiber membrane of the same composition. Owing to its desired oxygen permeability and good stability, the supported planar YSZ–LSCrF membrane developed in the present study holds promise for applications in chemical reactors integrating oxygen separation and oxygen-consuming chemical reactions such as partial oxidation of methane (POM). The phase inversion tape casting method explored in the present study can be applied to the preparation of other ceramic membranes.

Preparation of yttria stabilized zirconia membranes on porous substrates by a dip-coating process

Preparation of Yttria Stabilized Zirconia Ultrafiltration Membranes with Inorganic Precursors

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

Sol-Gel Synthesis of Yttria Stabilized Zirconia Membranes Through Controlled Hydrolysis of Zirconium Alkoxide

Preparation and Characterization of Highly Permeable Porous Yttria-Stabilized Zirconia Hollow Fiber Membrane

Dispersion and Stability of 8 Mol.% Yttria Stabilized Zirconia Suspensions for Dip-Coating Filtration Membranes

Highly permeable porous YSZ hollow fiber membrane prepared using ethanol as external coagulant

Preparation Of Ysz Microporous Membranes On Porous Alpha-Alumina With Metal Chlorides As Precursor

Preparation and Characterization of Three-Dimensionally Ordered Macroporous Yttria-Stabilized Zirconia by Aqueous Organic Gel Route

Preparation of Porous YSZ Monoliths via Sol-gel Process Accompanied by Phase Separation

Study on Gas Permeation Behaviour Through Atmospheric Plasma-Sprayed Yttria Stabilized Zirconia Coating

Preparation of unidirectional porous yttria stabilized zirconia ceramics by an alginate self assemble method

Preparation of YSZ electrolyte coatings for SOFC by electron beam physical vapor deposition combined with a sol infiltration treatment

Preparation of La_(0.8)Sr_(0.2)Cr_(0.5)Fe_(0.5)O_(3-δ)-Zr_(0.84)Y_(0.16)O_(1.92) Asymmetric Ceramic Oxygen-Permeable Membrane by Gelcasting

Preparation of electrolyte membranes for micro tubular solid oxide fuel cells

Preparation and Characterization of Porous YSZ-Al_2O_3 Comp Osite Membrane

Study on YSZ Membrane Electrolyte Fuel Cells Supported on Anode by Double-Layer Dry Pressing Method

Phase Inversion Tape Casting and Oxygen Permeation Properties of Supported Planar Zr0.84Y0.16O1.92–La0.8Sr0.2Cr0.5Fe0.5O3 − Δ Composite Membrane

Modification of Microstructure and Electrical Conductivity of Plasma-Sprayed Ysz Deposit Through Post-Densification Process

Sandwich-like Symmetric Dual-Phase Composite Membrane with an Ultra-Thin Oxygen Separation Layer and Excellent Durability

Effects of pyrolytic carbon on carburization strengthening and corrosion of 3YSZ hollow fiber membranes